Large-area multifunctional electro-chromic-chemical device made of W17O47 nanowires by Zn2+ ion intercalation

Qi Zhao,Jinkai Wang,Xinghui Ai,Zhenghui Pan,Feng Xu,John Wang,Yanfeng Gao

DOI: https://doi.org/10.1016/j.nanoen.2021.106356

IF: 17.6

2021-11-01

Nano Energy

Abstract:Both electrochromic and electrochemical processes have been widely investigated separately for respective energy saving and storage technologies. It would be of considerably value to effectively integrate the dual functionalities into a single multifunctional electro-chromic-chemical device (MED) capable of both. Herein, having considered the well theoretical capacity (820 mAh g−1), cost-effectiveness and high safety, we report the successful fabrication of MED in large area made of W17O47 nanowires, where Zn2+ ion intercalation takes place in the oxygen-vacant monoclinic tungsten oxide with WO polyhedral. The MED electrode materials demonstrate excellent cycling stability, large optical modulation (∆T) and high capacitance, when the polyhedron-enclosed interstitial sites form tunnels that facilitate Zn2+ ion diffusion, yielding a high specific capacitance (353.8 F g−1 at 0.5 A g−1) and a quite large optical modulation (∆T = 83.2% at 633 nm). With NaWO3 as a minor phase together with W17O47 nanowires, our density functional theory (DFT) calculations reveal a robust W17O47/NaWO3 interface structure, which leads to a desirable cycling stability (still maintaining 74.3% of its original optical modulation after 4000 cycles). The large-area MEDs assembled with W17O47/NaWO3 electrodes exhibit excellent energy-saving and energy-storage properties. For example, the temperature of an inner room equipped with the MED (30.5 cm × 26 cm) is 18.3 °C lower than that of a room equipped with blank glass, suggesting that the amount of irradiation is shielded significantly. Two series-connected MEDs (each size: 15 cm × 10 cm) is demonstrated to light up 4 light-emitting diodes (LEDs, 1.8–2.6 V) for more than 35 min

materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology