High-performance electrochromic WO 3 /POM–MXene energy storage device with color-based energy indication
Yanyan Yang,Yingying Song,Yue Qi,Bo Fu,Fengru Li,Huiwen Shi,Xiaoyang Yu,Shuping Liu,Xiaoshu Qu
DOI: https://doi.org/10.1016/j.surfin.2024.104397
IF: 6.2
2024-05-05
Surfaces and Interfaces
Abstract:Electrochromic energy storage devices (EESDs) with quantitative color-based visualization of their energy state have applications in smart displays and wearable intelligent electronics, as well as energy-efficient buildings. In addition, because of their ability to display their energy storage state accurately and in real time, the overcharging of energy-storage devices can be prevented, thus improving safety. WO 3 is a classical electrochromic material, but EESDs based on WO 3 can suffer from low coloration efficiencies and energy densities, as well as short cycle lives. However, compositing is a promising way to improve these properties. Therefore, in this study, an electrochromic WO 3 nanoblock (NB)/Preyssler-type K 12.5 Na 1.5 [NaP 5 W 30 O 110 ]-15H 2 O polyoxometallate (P 5 W 30 )//Ti 3 C 2 T X MXene energy storage device was prepared by a simple hydrothermal method. The WO 3 NB/P 5 W 30 film was first deposited on a conductive substrate as the cathode and subsequently modified with the MXene film as the anode. The device exhibited a high coloration efficiency (145.02 cm 2 /C), excellent energy density (9.8 × 10 −3 mWh/cm 2 ), long cycle life (62.5 % retention rate after 5000 galvanostatic charge–discharge cycles), and excellent chromaticity difference (Δ E* , 25.91). These properties are not only due to the unique 2D layered structure of MXene but also the greater compatibility between the cathode and the anode (as shown by the q -values). In addition, compared to a WO 3 NB film alone, the composite WO 3 NB/P 5 W 30 film had higher areal capacitance (12-times higher) and Δ E* (11-times higher), which is attributed to the synergism between the crystalline WO 3 and amorphous polyoxometallate composite. This study provides an effective method for developing high-performance EESDs with quantitative color-based charge-state visualization and long cycle lives.
materials science, coatings & films,physics, applied,chemistry, physical, condensed matter