Abstract:With inspiration from the structure of macromolecular thioether generated in the 9H-xanthene-9-thione mediated radical polymerization, five thioethers containing 9-alkyl-9-phenylthio/methylthio-xanthene structure were synthesized. Xanthydrol was selected as the precursor for two 9-substituted xanthene intermediates. 9-(Phenylthio)-9H-xanthene was obtained via a condensation reaction between xanthydrol and thiophenol in the presence of perchloric acid as catalyst. 9-(Methylthio)-9H-xanthene was obtained via the thioetherification of the chlorinated product of xanthydrol with sodium methyl mercaptide. The sulfurated intermediates were deprotonated by n-butyl lithium, and transformed into five target products via substitution reactions with three alkyl halides individually. H-1-NMR, C-13-NMR, FTIR and UV-Vis analyses were conducted to confirm and characterize the thioethers. Afterwards, a systematic study on the polymerization behavior of styrene (St) initiated by the thioethers was carried out in the absence and presence of a thermal initiator. Bulk polymerizations of St were initiated successfully by the thioethers at 80 degrees C with relatively low monomer conversions, and the reactions exhibited uncontrolled polymerization behaviors without obvious increase in number-average molecular weight (M-n) in the polymerization process with the PDI of polymeric products above 3.0. However, when the thioethers were used together with 2,2'-azobis(2,4-dimethyl) valeronitrile (ABVN) in the solution polymerization of St in toluene at 65 degrees C, higher monomer conversions compared with those of bulk polymerization and certain controllability could be achieved, reflected by a linear increase in M-n with conversion. Besides, the effects of molar ratio of ABVN to thioether and reaction temperature on the polymerization behavior of St were investigated in detail. A reduction in the molar ratio of ABVN to thioether would cause a reduction in the concentration of propagating radicals, and lead to a decrease in monomer conversion. But the PDI of polymeric product narrowed down indicating a controllable polymerization. Furthermore, elevated reaction temperature brought about an increased concentration of chain radical, and resulted in a relatively low M-n with a broadened PDI.

Enhancing Adhesion Properties of Commodity Polymers through Thiol-Catechol Connectivities: A Case Study on Polymerizing Polystyrene-Telechelics via Thiol-Quinone Michael-Polyaddition

Compatibilizing Efficiency of Copolymer Precursors for Immiscible Polymer Blends

A New Strategy of Post-Polymerization Modification to Prepare Functionalized Poly(disubstituted Acetylenes)

Broadening the Chemical Space of Mussel-Inspired Polymerization: The Roll-out of a TCC-Polymer Platform with Thiol–Catechol Connectivities

Synthesis Of Sulfur-Containing Polyacetylenes And Fabrication Of Their Hybrids With Zno Nanoparticles

In Situ Compatibilization of Polypropylene and Polystyrene-Grafted Nano-Sized TiO2 in the Presence of Friedel–Crafts Catalyst

Synthesis of Precision Polymers with Regularly Placed Perfluoroalkyl Segments and Sulfonic Acid Groups Via ADMET Polymerization and Internal Alkene Modification

Organocatalyzed Chemoselective Ring-Opening Polymerizations.

Anionic Synthesis of Mono- and Heterotelechelic Polystyrenes via Thiol--Ene ``Click'' Chemistry and Hydrosilylation

Synthesis, Characterization and Quantitative Epoxidation-Modification of a Novel High-Transparency S(SP)S Symmetrical Triblock Copolymer with Alternating Mid-Block by LAP Method

Synthesis and Microphase Separation Behavior of Random, Mixed Cylindrical Brush Copolymers Bearing Polystyrene and Poly(ε-caprolactone) Side Chains

Preparation of a Novel Styrene Copolymer: Simultaneously Improving the Thermal Stability and Toughness

Precision ADMET Polyolefins Containing Dithiane: Synthesis, Thermal Properties, and Macromolecular Transformation

Surface Modification of Polystyrene Latex Particles Via Atom Transfer Radical Polymerization

Synthesis, kinetic study and characterization of C5 ‐dienes/styrene copolymers via living anionic polymerization in cyclopentyl methyl ether solvent

Mechanistic Study of Regio-Defects in the Copolymerization of Propylene Oxide/Carbonyl Sulfide Catalyzed by (salen)crx Complexes

aracterization of novel dumbbell shaped copolymers poly ( ethylene oxide ) xb-polystyrene-b-poly ( ethylene oxide ) x with tunable side arms by combination of e ffi cient thiol-ene addition reaction with living polymerization mechanism

Epoxidation modification of strictly alternating copolymer via living and controlled anionic alternating copolymerization of 1,3-pentadiene and styrene derivatives

Synthesis and Properties of Poly(p-Phenylene Terephthalamide) Bearing Both Polar and Unsaturated Substituents Introduced Via Claisen Rearrangement Reaction

Synthesis of Thioether Compounds and Their Application in Initiating/Controlling the Radical Polymerization of Styrene

Catalyst-Free Click Polymerization of Thiol and Activated Internal Alkynes: A Facile Strategy toward Functional Poly(β-thioacrylate)s