Abstract:The work is aimed at the development of an energy-saving technique involving the partial carboxylation of powdered lignocellulose products from the straw of annual agricultural plants and the use of the obtained products in rubber compositions as a water-swelling filler. Lignocellulosе powder from oat straw (composition: ɑ-cellulose—77.0%, lignin—3.8%, resins and fats—1.8%) was used for carboxylation without preliminary separation into components. Microwave radiation was used to activate the carboxylation process. This reduced the reaction time by 2–3 times. The synthesized products were analyzed by IR spectroscopy, thermogravimetry and scanning electron microscopy. Industrial product sodium carboxymethylcellulose (Na-CMC) was used as a swelling filler for comparison. The swelling fillers were fractionated by the sieve method; particles with the size of 0–1 mm were used for filling rubber compounds. The amount of swelling filler was 150 parts per 100 parts of rubber (phr). Due to the high filling of rubber compounds, plasticizer Oxal T-92 was added to the composition of a number of samples to facilitate the processing and uniform distribution of ingredients. The rubber composition was prepared in two stages. In the first stage, ingredients without swelling filler were mixed with rubber on a laboratory two-roll mill to create a base rubber compound (BRC). In the second stage, the BRC was mixed with the swelling filler in a closed laboratory plasti-corder rubber mixer, the Brabender Plasti-Corder® Lab-Station. Vulcanization was carried out at 160 °C. For the obtained samples, the physical-mechanical and sorption properties were determined. It has been shown that the carboxylated powdered lignocellulose from oat straw increases the strength properties of rubber in comparison with Na-CMC. It has been shown that when the carboxylated powdered lignocellulose from oat straw is introduced into the rubber composition, the degree of rubber swelling in aqueous solutions of various mineralizations increases by 50 and 100% in comparison with a noncarboxylated lignocellulose.

Physical-mechanical Properties and Morphology of Lignocellulose Powder Modifiers for Vulcanized Rubbers

Influence of Partially Carboxylated Powdered Lignocellulose from Oat Straw on Technological and Strength Properties of Water-Swelling Rubber

Modification of the Filler based on Kaolin and its Use in the Polymer Composites

Natural Fiber Fillers and their Influence on the Properties of Rubber

Structure and Properties of Modified Rubber Powder/Natural Rubber Blends

Preparation And Mechanical Properties Of Natural Rubber Powder Modified By Carbon Nanotubes

Improvement of the mechanical property and thermal stability of polypropylene/recycled rubber composite by chemical modification and physical blending

Sulfur and peroxide curing of NBR based rubber compounds filled with kraft lignin and calcium lignosulfonate

Enhanced Actuation Strains of Rubber Composites by Combined Covalent and Noncovalent Modification of TiO2 Nanoparticles

Effect of Carbon Black Nature on Vulcanization and Mechanical Properties of Rubber

Preparation and Properties of Powder Styrene-Butadiene Rubber Composites Filled with Carbon Black and Carbon Nanotubes

Hyperbranched dispersant modification of sisal cellulose based on hydrogen bonding interactions for strengthening natural rubber composite

Technology of CTC-IPN modified scrap rubber powder

Influence of Prolonging Vulcanization on the Structure and Properties of Hard Rubber

Use of Lignin-Based Crude Carbon Dots As Effective Antioxidant for Natural Rubber.

Hydrophobic modification of lignin for rubber composites

Polymeric compounds based on thermoplastic elastomer styrene-butadiene-styrene block copolymers and siliconic rubber powder

Study on Properties of Natural Rubber Reinforced by Poly(Sodium-4-Styrenesulfonate)-Decorated Carbon Black with A Latex Compounding Technique

Development of resin/waster rubber powder thermoplastic elastomer

Cellulose and lignin in place of EPDM and carbon black for automotive sealing profiles

Effect of amounts of carbon black doped with samarium oxide on properties of powdered natural rubber