Abstract:To investigate the coupling between nuclear and electronic energy losses in UO 2 , we irradiated thin foils with 0.39 MeV Xe and/or 6 MeV Si ions at 93 K using single or simultaneous dual beam ion irradiations. The evolution of perfect dislocation loops was characterized by in situ transmission electron microscopy (TEM). Additional ex situ TEM characterizations at room temperature revealed for the first time in UO 2 the presence of faulted Frank loops too small to be measured during in situ experiments and conventional bright field kinematical imaging conditions. For the single Xe irradiation, which favor dominant ballistic energy losses, we observed a continuous nucleation of small perfect dislocation loops, which increase in size for our last fluences by growing through mainly coalescence effect. Both the single Si and dual Xe & Si irradiations showed a coupling between nuclear and electronic energy losses, resulting in a significant loop density increase and a tangled line network formation, respectively. These phenomena occur at lower dpa levels, compared to the single Xe irradiation, likely resulting from the thermal spike effect of Si ions. The present results were compared to our previous work at 293 K to investigate the role of irradiation temperature on the energy losses coupling. For the Xe irradiation, the density increases and the loops are smaller at 93 K compared to 293 K, resulting from the uranium interstitials mobility being prevented or allowed. For the Si irradiation, the dislocation evolution kinetics are similar at both temperatures. The electronic excitations effect seems greater than the irradiation temperature effect in this temperature range. For the Xe & Si irradiation, the loop kinetics change resulting in a tangled line network formation is faster and thus the loop transformation into lines occurs at lower dpa levels at 93 K compared to 293 K. It appears that the irradiation temperature affecting the mobility of some small point defects reduces the electronic excitation effect in this case.

Evolution of extended defects in UO 2 during high temperature annealing

Molten uranium dioxide structure and dynamics

The role of xenon/krypton adsorption on the growth of intra-granular bubbles in irradiated UO2

Determination of Thermal Expansion, Defect Formation Energy, and Defect-Induced Strain of α-U Via ab Initio Molecular Dynamics

Evolution of dislocation loops in irradiated α-Uranium: An atomistically-informed cluster dynamics investigation

Effect of Radiation Defects on Thermo–Mechanical Properties of UO2 Investigated by Molecular Dynamics Method

Influence of thermal effect on dislocation loop evolution in Fe+-irradiated CeO2 during in-situ annealing

Molecular dynamics simulations of microstructural evolution of irradiated (U,Pu)O2 studied via simulated XRD patterns

Microstructural Evolution of Gas Bubbles and Thermal Conductivity in UO2-BeO Bicrystal

Effect of Annealing Temperature on Dislocation Loop Absorption And Evolution in Fe by Molecular Dynamics Study

Differences in coupling between nuclear and electronic energy losses in UO 2 with irradiation temperature: an in situ TEM study

In-situ TEM investigation of defect evolution in FeCrAl during post-irradiation annealing

The evolution and interaction of irradiation defects in CeO2 during H2+ & He+ dual-beam synergistic irradiation investigated by in-situ TEM

Swelling Mechanism of Lattice with the Ingrowth of the Defects in UO2

The Role of Temperature on Irradiation Defect Evolution near Surfaces and Grain Boundaries in Tungsten

Effect of Grain Size on Irradiation-Induced Bubble Evolution in High Burn-Up UO2: A Phase-Field Study

Effect of Grain Size on Irradiation-Induced Bubble Evolution in High Burn-Up UO2: 2: A Phase-Field Study

First-principles study on oxidation effects in uranium oxides and high-pressure high-temperature behavior of point defects in uranium dioxide

The Evolution of Structural Defects under Irradiation in W by Molecular Dynamics Simulation

Micro-defects evolution of (Al0.33Cr0.21Fe0.28Zr0.18)O2 and (Al0.33Cr0.2Mn0.09Fe0.22Zr0.16)O2 induced by hydrogen ions irradiation

Examining the Effects of Irradiation Temperature on Defect Generation and the Nature of Dislocation Loops