Revealing electrochemical performance of Ni doping LiFePO4 composite

Li, Yin

DOI: https://doi.org/10.1007/s12034-024-03295-0

IF: 1.878

2024-10-19

Bulletin of Materials Science

Abstract:In this work, Ni 2+ was doped into the crystal lattice of LiFePO 4 to improve the electrochemical performance. Lengths of the Li–O bonds in LiFe 0.98 Ni 0.02 PO 4 /C (2% NiSO 4 -doped LiFePO 4 ) is longer than that of the bare LiFePO 4 sample, the micromorphology of LiFe 0.98 Ni 0.02 PO 4 /C sample becomes uniform, and the Ni 2+ doped into LiFePO4 expands the crystal plane spacing, which is conducive to Li + diffusion. Amongst all the doped samples, the Li + diffusion coefffcient of LiFe 0.98 Ni 0.02 PO 4 /C is the largest, and the redox peak of LiFe 0.98 Ni 0.02 PO 4 /C is more symmetrical, sharper and narrower, indicating that the proper amount of Ni 2+- modified LiFePO 4 can improve the electrochemical performance. Specific discharge capacity at 1C is 152 mAh g −1 when the doping amount is 2%. Additionally, after 200 cycles at 2C, the discharge specific capacity can be attained at 140 mAh g −1 and capacity retention rate reached 98%.

materials science, multidisciplinary