Enhanced interfacial bonding strength between metal and polymer via synergistic effects of particle anchoring and chemical bonding

Xin Zou,Bakytzhan Sariyev,Ke Chen,Muyang Jiang,Min Wang,Xueming Hua,Lanting Zhang,Aidang Shan
DOI: https://doi.org/10.1016/j.jmapro.2021.05.058
IF: 5.684
2021-08-01
Journal of Manufacturing Processes
Abstract:<p>To enhance the performance of metal-polymer joint, surface modification is normally applied. Different from the common methods of increasing roughness or manufacturing complicated patterning, a new strategy of microscale morphology design of low roughness surface was introduced in this work, for improving the interfacial bonding strength between Ti6Al4V titanium alloy (TC4) and polyethylene terephthalate (PET) joined by hot pressing method. Low-roughness (R<sub>a</sub> = 0.18 μm) surface achieved by HF etching can also significantly enhance the interfacial bonding strength of TC4-PET joint by 133%, from 4.5 MPa (as-polished) to 10.5 MPa, as high as the joint strength achieved by sandblasting (11 MPa) with much higher roughness (R<sub>a</sub> = 3.7 μm). The bonding mechanisms in joints with different surface treatments were investigated and compared, showing that a new effect of surface particle anchoring played a key role in enhancing the interfacial bonding. Based on the characterization results and analyses, the crack propagation paths of HF and HNO<sub>3</sub>-HF treated samples were clarified and illustrated. This study indicated that roughness is not the only decisive factor of joint strength and demonstrated a new effective strategy via synergistic effects of surface particle anchoring and chemical bonding to improve interfacial bonding of metal and polymer from both theoretical and practical points of view.</p>
engineering, manufacturing
What problem does this paper attempt to address?
This paper attempts to solve the problem of insufficient interfacial bonding strength of metal - polymer joints in practical applications. Specifically, the researchers focus on how to improve the interfacial bonding strength between titanium alloy (Ti6Al4V, namely TC4) and polyethylene terephthalate (PET) through surface modification techniques. Traditional methods for improving interfacial bonding strength usually rely on increasing surface roughness or creating complex surface patterns, but these methods may not be suitable for application scenarios where a low - roughness surface needs to be maintained. To overcome this challenge, the paper proposes a new strategy, that is, enhancing the interfacial bonding strength between TC4 and PET by designing a low - roughness surface with micro - scale morphology. This method not only considers the role of surface particle anchoring but also explores the synergistic effect of chemical bonding. The experimental results show that the low - roughness (Ra = 0.18 μm) surface obtained by hydrofluoric acid (HF) etching can significantly improve the interfacial bonding strength of TC4 - PET joints, from 4.5 MPa without treatment to 10.5 MPa, almost the same as 11 MPa obtained by sandblasting treatment (Ra = 3.7 μm). This indicates that roughness is not the only factor determining joint strength, and the synergistic effect of surface particle anchoring and chemical bonding can effectively improve the interfacial bonding strength between metals and polymers. In addition, the paper also analyzes in detail the influence of different surface treatment methods on the mechanical properties of joints, and explores the fracture mechanism and bonding mechanism of joints through characterization means such as SEM and XPS. These research results provide new ideas and technical approaches for the development of high - performance metal - polymer composites.