Single nucleation of Cl-doped FAPbBr3 with inhibited ion migration for ambipolar radiation detection

Quanchao Zhang,Xin Liu,Xin Zhang,Zijian Wang,Baoqiang Zhang,Yingying Hao,Alain Dubois,Wanqi Jie,Yadong Xu

DOI: https://doi.org/10.1039/d3ta06640a

IF: 11.9

2023-12-19

Journal of Materials Chemistry A

Abstract:Compared with the MAPbBr 3 single crystals (SCs), FAPbBr 3 possesses a better chemical and structural stability and is expected to be a promising organic–inorganic candidate for next-generation room-temperature radiation materials. However, challenges of FAPbBr 3 bulk crystals remain yet, such as numerous nuclei and the intrinsic stability issue, limiting further performance development and large-scale commercialized production. Herein, we report the growth of Cl-doped FAPbBr 3 SCs using an inverse temperature crystallization method and realize single nucleation without a seed. The resulting FAPbBr 2.9 Cl 0.1 presents the longest carrier lifetime compared with other components, which reveals the lowest trap-state density. As-grown FAPbBr 2.9 Cl 0.1 also exhibits a high resistivity of 4.13 × 10 9 Ω cm, comparable hole and electron mobility-lifetime products of (1.5–2.1) × 10 −4 cm 2 V −1 , and a high activation energy ( E a ) of 0.58 eV, yielding excellent charge transport and collection. Additionally, the AZO/FAPbBr 2.9 Cl 0.1 /Au device structure markedly reduces leakage current, resulting in a superior I ON / I OFF ratio of 22 240 at a bias of 30 V, and distinguishable 241 Am α-particle pulse height spectra were observed for both electrons and holes with an energy resolution of 19.2% and 21.3%, respectively. These results demonstrate the great potential of FAPbBr 2.9 Cl 0.1 SC as a radiation material.

materials science, multidisciplinary,chemistry, physical,energy & fuels