Ultralarge All‐Inorganic Perovskite Bulk Single Crystal for High‐Performance Visible–Infrared Dual‐Modal Photodetectors

Qingzhi Cui,Tian Tian,Jianhai Li,Yue Wang,Yuhui Dong,Jiayue Xu,J. Xue,Jizhong Song,Leimeng Xu,H. Zeng,Handong Sun

DOI: https://doi.org/10.1002/adom.201700157

2017-06-01

Abstract:Visible‐infrared dual‐modal light harvesting is crucial for various optoelectronic devices, particularly for solar cells and photodetectors. For the first time, this study reports on large 25 cm3‐volume all‐inorganic perovskite CsPbBr3 single crystal (SC) with an emphasis on the observed visible‐infrared dual‐modal light harvesting and sensing as demonstrated by the high‐performance visible‐infrared dual‐modal photodetectors. First, ultralarge 25 cm3‐volume CsPbBr3 SC ingots with trapping state density as low as of 1 × 109 cm−3 have been achieved by a modified Bridgman growth method. The volume reported here is the largest CsPbX3 (X = Cl, Br, I) all‐inorganic perovskite system up to now, and the SC can be facilely cut into SC wafers with a diameter of 25 mm for various optoelectronic devices. Furthermore, these CsPbBr3 SCs exhibit a visible absorbance coefficient, a near‐infrared (IR) two‐phonon absorption coefficient, a carrier diffusion length, and a mobility as high as of 105 cm−1, 3.7 cm per Goeppert‐Mayer (GM), 10 µm and 2000 cm2 V−1 s−1, respectively. These merits match well to the requirements of high‐performance Vis‐IR dual‐modal light harvesting optoelectronic devices, which has been demonstrated by the CsPbBr3 SC photodetectors operated under the irradiation of both visible and IR light sources with light on/off ratio higher than 103. These results demonstrate the CsPbBr3 SCs with high visible‐infrared dual‐modal light harvesting capability and excellent electrical transporting properties have a huge potential in various optoelectronic devices, such as solar cells, photodetectors, and lasers.

Engineering,Physics,Materials Science