Delayed Crystallization Kinetics Allowing High‐Efficiency All‐Polymer Photovoltaics with Superior Up‐Scaled Manufacturing
Tianyi Chen,Xiangjun Zheng,Di Wang,Yuxuan Zhu,Yanni Ouyang,Jingwei Xue,Mengting Wang,Shanlu Wang,Wei Ma,Chunfeng Zhang,Zaifei Ma,Shuixing Li,Lijian Zuo,Hongzheng Chen
DOI: https://doi.org/10.1002/adma.202308061
IF: 29.4
2023-09-23
Advanced Materials
Abstract:Though encouraging performance has been achieved in small‐area organic photovoltaics (OPVs), reducing efficiency loss when evoluted to large‐area modules is an important but unsolved issue. Considering that polymer materials show benefits in film‐forming processability and mechanical robustness, a high‐efficiency all‐polymer OPV module has been demonstrated in this work. First, a ternary blend consisting of two polymer donors, PM6 and PBQx‐TCl, and one polymer acceptor, PY‐IT, was developed, with which triplet state recombination was suppressed for a reduced energy loss, thus allowing a higher voltage; and donor‐acceptor miscibility was compromised for enhanced charge transport, thus resulting improved photocurrent and fill factor, all these contributed to a champion efficiency of 19% for all‐polymer OPVs. Second, the delayed crystallization kinetics from solution to film solidification was achieved that gives a longer operation time window for optimized blend morphology in large‐area module, thus relieving the loss of fill factor and allowing a record efficiency of 16.26% on an up‐scaled module with an area of 19.3 cm2. Besides, this all‐polymer system also showed excellent mechanical stability. Our work demonstrates that all‐polymer ternary systems are capable of solving the up‐scaled manufacturing issue, thereby enabling high‐efficiency OPV modules. This article is protected by copyright. All rights reserved
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology