Abstract:Targeting the removal of Pb2+ in wastewater, cellulosic materials were carbonized in an aerobic environment and activated via ion exchange. The maximum adsorption capacity reached 243.5 mg/g on an MCC-derived adsorbent activated with sodium acetate. The modified porous properties improved the adsorption capacity. The capacity could be completely recovered five times through elution with EDTA. Because of the negative effects of Ni, Mg, and Ca elements, the adsorption capacities of activated carbonized natural materials were lower than that of pure cellulose. N2 adsorption measurement showed that the adsorbent had a large specific surface area as well as abundant micropores and 4-nm-sized mesopores. FTIR and surface potential results proved that carboxyl group was generated in the aerobic carbonization, and was deprotonated during ion exchange. This adsorbent consisted of C-C bonds as the building blocks and hydrophilic groups on the surface. XPS results demonstrated that the Pb 4f binding energies were reduced by 0.7-0.8 eV due to the interaction between Pb2+ and the activated adsorbent, indicating that the carboxylate groups bonded with Pb2+ through coordination interactions. Pseudo-second-order and Elovich kinetic models were well fitted with the adsorption processes on the pristine and activated carbonized adsorbents, indicative of chemisorption on heterogeneous surfaces. The Freundlich expression agreed well with the data measured, and the pristine and activated adsorbents had weak and strong affinities for Pb2+, respectively. The Pb2+ adsorption process was exothermic and spontaneous, and heat release determined the spontaneity. The adsorption capacity is attributed to the carboxylate groups and pores generated in the aerobic oxidation and ion exchange procedures.

Adsorptive removal of beryllium by Fe-modified activated carbon prepared from lotus leaf

Beryllium adsorption from beryllium mining wastewater with novel porous lotus leaf biochar modified with PO43−/NH4+ multifunctional groups (MLLB)

Preparation of porous calcium carbonate biochar and its beryllium adsorption performance

Effect of mechanical−chemical modification on adsorption of beryllium by calcite

Preparation of Fe-loaded Activated Carbon and Its Adsorption Property of U(VI) in Aqueous Solution

Adsorptive Removal of Pb(II) by Magnetic Activated Carbon Incorporated with Amino Groups from Aqueous Solutions

Effect of Oxidation Treatment on the Adsorption and the Stability of Mercury on Activated Carbon.

Enhanced adsorption of Pb2+ by the oxygen-containing functional groups enriched activated carbon

Composite hydrogel derived iron/nitrogen co-doped carbon for bisphenol A removal

Preparation of Lotus Root-Type Monolithic-Activated Carbons with an Hierarchical Pore Structure from Rice Husks and Their Adsorption of Vitamin B12.

Low-temperature aerobic carbonization and activation of cellulosic materials for Pb2+ removal in water source

Adsorption behavior of Ni (II) on lotus stalks derived active carbon by phosphoric acid activation

Removal of bromate from water using modified activated carbon

Adsorption of gaseous elemental mercury with activated carbon impregnated with ferric chloride

Biosorption Behavior and Mechanism of Beryllium from Aqueous Solution by Aerobic Granule

Β-Feooh-coupled Activated Carbon Prepared by the High Temperature Impregnation Method for Bromate Removal from Water

Aqueous mercury and lead removal with activated carbons derived from high sulfur carbonaceous materials

Application of Mg-Fe Layered Double Hydroxides/Biochar Composite for the Removal of La(III) from Aqueous Solutions

Removal of Pb(II) from water using nanoscale SBA-15

Activation of Firmiana Simplex Leaf and the Enhanced Pb(II) Adsorption Performance: Equilibrium and Kinetic Studies.

Competitive adsorption characteristics of VOCs and water vapor by activated carbon prepared from Fe/N-doped pistachio shell