Abstract:A series of NaGd(0.99-x%)F4: 1% Bi3+, x% Eu3+ (x = 0-50) and NaGd(1-x%)F4: x% Eu3+ (x = 0-50) nanocrystals (denoted as NGBF-x% Eu3+ and NGF-x% Eu3+, respectively) have been synthesized by hydrothermal method. The influence of Bi3+ and Eu3+ on microstructures and luminescence properties of the products are deeply investigated. The TEM results display that all the obtained products are irregular polyhedrons with a diameter in a range from 30 to 80 nm with the increasing substitution concentration of Eu3+. It was found that the introduction of Bi3+ hardly affects the morphology and size of the obtained products. Under the excitation of 393 nm NUV, all samples exhibit the typical emission of Eu3+ ions with main red and yellow emissions centered at 616 and 591 nm, respectively. After doping a small amount of Bi3+ ions, the largest emission intensity of the characteristic emissions of Eu3+ for the gained NGBF-x% Eu3+ nanocrystals appeared at x = 0.2, whereas it observed at x = 0.3 for the obtained NGF-x% Eu3+ nanocrystals. It is obviously that the introduction of 1% Bi3+ ions not only increases the emission intensity of Eu3+ ions significantly, but also reduces the doping concentration of Eu3+. Especially, studied NGBF-20% Eu3+ phosphor exhibits excellent stand up to thermal impact during thermal cycling between 298 and 473 K. A WLED device by merging a NUV chip, NGBF-20% Eu3+ phosphor and commercial (Sr,Ba)(2)SiO4: Eu2+ green phosphor/BaMgAl10O17: Eu2+ blue phosphor possesses suitable correlated color temperature (CCT, 7395 K) and high color rendering index (CRI, 90.8%). These results unambiguously show that the NGBF-x%Eu3+ nanocrystals are promising candidate for applications in WLEDs. (C) 2020 Elsevier B.V. All rights reserved.

Improving the blue emission from Eu2+ by codoping Re3+ ions (Re Y, La, Gd, Lu) in NaMgPO4

Energy-transfer and charge-compensation jointly improved the luminescence of NaMgPO4:Eu2+,Tb3+ phosphor

Effects of Re3+ (re = Y, La, Gd) Co-doping on Luminescence Properties of MSi2O2N2:Eu2+ (M = Ca, Sr) Phosphors

Crystal structural and photoluminescence properties of Eu3+ doped MgZn2(PO4)2 phosphors by R + (R=Li, Na, K) charge compensation

Enhancing the Emission Intensity and Decreasing the Full Widths at Half Maximum of Ba3Si6O12N2:Eu(2+) by Mg(2+) Doping.

Controllable Eu2+-Doped Orthophosphate Blue-/Red-Emitting Phosphors: Charge Compensation and Lattice-Strain Control

Influence of Co-Doping Different Rare Earth Ions on CaGa2S4: Eu2+, RE3+(RE=Ln) Phosphors

Site-selective occupation of Eu 3+ , high-quenching concentration, and enhanced luminescence via Mg 2+ co-doping in a borophosphate phosphor

Enhanced luminescence performance in double perovskite Na4/5Gd16/15-MgWO6: xEu3+ red-emitting phosphors for white LEDs through cation modification

Luminescence properties, tunable emission and energy transfer of Ca9MgLi(PO4)7:Bi3+/Eu3+ phosphor

Dual-channel Enhanced Luminescence of Double Perovskite NaGdMgWO6:Eu3+ Phosphor Based on Alternative Excitation and Delayed Quenching

Bi3+ Ion Doping: an Effective Strategy to Significantly Enhance Luminescence Performances of NaGdF4: Eu3+ Red-Emitting Nanocrystals

The Effects Of Rare-Earth Co-Dopants On Green Long-Lasting Phosphorescence And Thermoluminescence Properties Of Ca8mg(Sio4)(4)Cl-2:Eu2+,Re3+

Interrupting the long-range energy migration among Eu3+ by the introduction of unequivalent [NaO8] units to achieve both high quenching concentration and quantum yield in NaY2Ga2InGe2O12

Mechanisms of Li+ Ions in the Emission Enhancement of KMg4(PO4)3:Eu2+ for White Light Emitting Diodes.

Effect of Er3+ and Nd3+ doping on the luminescent properties of BaMgAl10O17:Eu phosphor

Garnet-based red emitting phosphors Li6MLa2Nb 2O12: Eu3+ (M=Ca, Sr, Ba): Photoluminescence improvement by changing crystal lattice

Improvement of Luminescence Performance of Single-Phase White-Emitting Na3Gd(PO4)2:Dy3+ Phosphor by Co-Doping with Eu3+

Design Principles for Achieving Red Emission in Eu2+/Eu3+ Doped Inorganic Solids

Tunable Luminescence Of Ceal11o18 Based Phosphors By Replacement Of (Alo)(+) By (Sin)(+) And Co-Doping With Eu

Enhanced red emission of Yb, Ho: NaYGd(WO4)2 phosphors by codoping Ce3+