Facile fabrication of PEDOT/PVDF composite membrane by vapor phase polymerization with excellent separation performance

Xiaoyu Wang,Zengchi Hu,Tao Cai,Rui Zhang,Xue Li,Jiangbin Xia

DOI: https://doi.org/10.1016/j.seppur.2024.128286

IF: 8.6

2024-06-19

Separation and Purification Technology

Abstract:The facile fabrication of high-performance polymer composite membranes poses a challenging task. Herein, poly (3, 4-ethylenedioxythiophene) (PEDOT) selective layer was deposited onto the surface of porous polyvinylidene fluoride (PVDF) substrate by a simple vapor phase polymerization (VPP) method, resulting in the fabrication of high-performance composite separation membrane PEDOT/PVDF. This composite membrane has excellent separation performance to separate model wastes in water systems. For instance, the rejection rates for differently charged neutral red (NR), azure II (Azu II), congo red (CR), and methylene blue (MB) were 99.1 ± 0.2 %, 99.2 ± 0.2 %, 99.4 ± 1.5 %, and 97.9 ± 1.0 %, respectively, with corresponding permeances of 42.3 ± 2.4 L m −2 h −1 bar −1 , 60.1 ± 1.9 L m −2 h −1 bar −1 , 25.1 ± 5.6 L m −2 h −1 bar −1 , and 68.2 ± 4.9 L m −2 h −1 bar −1 . PEDOT/PVDF composite membrane demonstrated excellent chemical stability, and the rejection rate of NR decreased by only 4.1 % during 48 h of continuous filtration. In the environment of NR solution (50 ppm) at 60 °C or Azu II-NaOH solution (pH 13), it maintained high selectivity (>96 %) while significantly improving permeability (>80 L m −2 h −1 bar −1 ). The entire fabrication process of high-performance PEDOT/PVDF membrane was conducted at room temperature, with high versatility simple operation and minimal equipment requirement, offering significant advantage compared to similar reported membrane materials. This work provides a useful reference for the facile fabrication of high-performance separation membranes.

engineering, chemical