Abstract:The use of poly(vinylidene fluoride) (PVDF) microfiltration (MF) membranes to purify oily water has received much attention. However, it is challenging to obtain high-performance PVDF microfiltration membranes due to severe surface fouling and rapid decline of permeability. This study explored a new approach to fabricate high-performance PVDF/silica (SiO2) composite membrane via the use of a polymer solution featuring lower critical solution temperature (LCST) characteristics and the non-solvent thermally induced phase separation method (NTIPS). Coupling with morphological observations, the membrane formation kinetics were analyzed in depth to understand the synergistic effect between the LCST solution properties and fabrication conditions in NTIPS. Utilizing such a synergistic effect, the transition from finger-like macrovoid pores to bi-continuous highly connected pores could be flexibly tuned by increasing the PVDF concentration and the weight ratio of SiO2/PVDF in the dope solution and by raising the coagulation temperature to above the LCST of the solution. The filtration experiments with surfactant-stabilized oil-water emulsion showed that the permeation flux of the PVDF/SiO2 composite membranes was higher than 318 L·m−2·h−1·bar−1 and the rejection above 99.2%. It was also shown that the PVDF/SiO2 composite membranes, especially those fabricated above the LCST, demonstrated better hydrophilicity, which resulted in significant enhancement in the anti-fouling properties for oil/water emulsion separation. Compared to the benchmark pure PVDF membrane in oily water purification, the optimal composite membrane T70 was demonstrated via the 3-cycle filtration experiments with a significantly improved flux recovery ratio (Frr) and minimal reduced irreversible fouling (Rir). Overall, with the developed method in this work, facile procedure to tune the membrane morphology and pore structure was demonstrated, resulting in high performance composite membranes suitable for oil/water emulsion separation.

Multifunctional PVDF-fabric-based bilayer membrane with wettability difference for efficient removal of direct dye from water and high-flux oil/water separation

Rational design of a super anti-fouling PVDF-PC-TBT@X membrane for emulsion/dye wastewater separation

PVDF-based nanofiber membrane decorated with Z-scheme TiO 2 /MIL-100(Fe) heterojunction for efficient oil/water emulsion separation and dye photocatalytic degradation

Composite membranes with multifunctionalities for processing textile wastewater: Simultaneous oil/water separation and dye adsorption/degradation

Bio-inspired Underwater Superoleophobic PVDF Membranes for Highly-Efficient Simultaneous Removal of Insoluble Emulsified Oils and Soluble Anionic Dyes

Facile fabrication of fabric-based membrane for adjustable oil-in-water emulsion separation, suspension filtration and dye removal

Fabrication of Anatase TiO2/PVDF Composite Membrane for Oil-in-Water Emulsion Separation and Dye Photocatalytic Degradation

High-Performance Pvdf Water Treatment Membrane Based on Il-Na+Mmt for Simultaneous Removal of Dyes and Oil-Water Emulsions

Fabrication of a superhydrophilic PVDF membrane with excellent chemical and mechanical stability for highly efficient emulsion separation

In-situ generation of anti-fouling TpPa/PVDF membranes showing excellent photocatalytic degradation and self-cleaning for dyes in water

A superhydrophilic and robust fabric, featuring self-assembled layers of chitosan and carbon nanotubes, facilitates high-throughput oil–water separation

Multifunctional polyacrylonitrile based nanofibrous membranes with pH-regulable surface charge for efficient separation of oil-in-water emulsions and controllable removal of dyes

Wodyetia bifurcate structured carbon fabrics with durable superhydrophobicity for high-efficiency oil-water separation

Construction of Gradient SA-TiO2 Hydrogel Coated PVDF-g-IL Fibre Membranes with High Hydrophilicity and Self-Cleaning for the Efficient Separation of Oil-Water Emulsion and Dye Wastewater

A Facile Method to Control Pore Structure of PVDF/SiO2 Composite Membranes for Efficient Oil/Water Purification

A superhydrophobic nanofiber membrane and its application to dye filtration using membrane distillation

Green Fabrication of Superhydrophilic/Underwater Superoleophobic Composite Membrane for High-Efficiency Oil/Water Separation in Harsh Environments

Multi-functional composite membrane with strong photocatalysis to effectively separate emulsified-oil/dyes from complex oily sewage

Improving multifunctional properties of the polyvinylidene fluoride (PVDF) membrane with crosslinked dialdehyde-starch (DAS) and polyethyleneimine (PEI) coating

One-Step Prepared Multifunctional Polyacrylonitrile/MIL-100(Fe) Membrane with High-Density Porous Fibers for Efficient Dye/Oil Wastewater Remediation

Dual-functional membrane decorated with flower-like metal–organic frameworks for highly efficient removal of insoluble emulsified oils and soluble dyes