An investigation of the effects of Nd 2 O 3 on the mechanical, structural, and optical properties of borosilicate glasses for optimizing radiation shielding performance
M.H.A. Mhareb
DOI: https://doi.org/10.1016/j.optmat.2024.116079
IF: 3.754
2024-09-11
Optical Materials
Abstract:A group of glasses with a composition, 5Li 2 O−(25-x) Bi 2 O 3 –10SiO 2 –45B 2 O 3 –15SrO−xNd 2 O 3 where x = 0, 0.5, 1, and 2 mol% was prepared to optimize shielding properties. The glass samples were coded as BiBNd0, BiBNd1, BiBNd2, and BiBNd3. Adding Nd 2 O 3 instead of Bi 2 O 3 reduced the density values, which are 5.098, 4.959, 4.930, and 4.859 g/cm 3 for BiBNd0, BiBNd1, BiBNd2, and BiBNd3 samples, respectively. Rising Nd 2 O 3 content also reduced the mechanical properties. For example, the Young's modulus values were 69.773, 68.327, 68.387, and 68.320 GPa for BiBNd0, BiBNd1, BiBNd2, and BiBNd3 samples, respectively, which were better than standard glasses of RS520 and RS360. The band gap values varied with the addition of Nd 2 O 3 , and their values were 2.848, 3.043, 2.613, and 2.665 eV for BiBNd0, BiBNd1, BiBNd2, and BiBNd3 samples, respectively. In addition, the absorption spectrum showed several absorption peaks related to Nd 2 O 3 due to the transition from the ground state (4I 9/2 ) to the excited state of 4 F 3/2 , ( 4 F 5/2 + 2 H 9/2 ), ( 4 F 7/2 + 4 S 3/2 ), 4 F 9/2 , 2 H 11/2 , ( 4 G 5/2 + 2 G 7/2 ), and ( 2 K 13/2 + 4 G 7/2 + 4 G 9/2 ). In addition, adding Nd 2 O 3 reduces the neutron and gamma shielding features. For instance, the linear attenuation coefficient (LAC) values of 0.622 MeV for BiBNd0, BiBNd1, BiBNd2, and BiBNd3 were 0.500, 0.485, 0.480, and 0.470 cm −1 , which were better than the RS323-G19 and RS360 and they competed with the RS520. At the same time, the transmission factor at 5 cm and 0.662 MeV was 0.082, 0.088, 0.090, 0.09, 0.082, 0.246, and 0.201 for BiBNd0, BiBNd1, BiBNd2, BiBNd, RS520, RS323-G19, and RS360, respectively. Adding Nd 2 O 3 instead of Bi 2 O 3 reduced the fast neutron removal cross-section from 0.108 to 0.104 cm −1 . Lastly, the current glasses showed promising gamma, neutron, and mechanical shielding features better than other standard glasses and materials used in the radiation shielding field.
materials science, multidisciplinary,optics