Growth and Temperature-Dependent Mechanical and Thermal Properties of One-Dimensional Chain Structure Hg 2 Br 2 Crystals for Infrared Acousto-Optic Device Application

Lin Liu,Rongzhen Li,Yanxiao Bi,Sheng-Qing Xia,Guodong Zhang,Xutang Tao

DOI: https://doi.org/10.1021/acs.cgd.1c00957

2021-11-16

Abstract:The long-wave infrared acousto-optic tunable filters (AOTFs) based on Hg2Br2 crystals have attracted much interest in space exploration and harmful chemical agent detection. However, the growth of large Hg2Br2 single crystals with high quality and optical homogeneity still remains a challenge, and the lack of temperature-dependent mechanical and thermal properties of this crystal hinders the further enhancement of acousto-optic performance in practical applications. In this context, Hg2Br2 crystals (Φ 35 × 40 mm3) were successfully grown by the physical vapor transport (PVT) method. The optical homogeneity of the as-grown crystal is increased to 7.15 × 10–5 by restraining the impurities, striations, and cracks. In addition, the anisotropic mechanical and thermal properties varying with the temperature of Hg2Br2 crystals were systematically investigated. The compression modulus along the ⟨110⟩ orientation decreases from 17 to 7 GPa in the temperature range of −100 to 150 °C, while it ranges from 5.5 to 1.5 GPa along the ⟨001⟩ orientation. The thermal conductivities along ⟨110⟩ and ⟨001⟩ orientations vary in the range of 1.32–0.52 and 2.06–1.05 W/(m·K) with the increase in temperature from −140 to 100 °C, respectively, and then remain stable in the range of 100–150 °C. Using the first-principles calculation on the electron transfer characteristic between atoms and the bonding property within molecules of Hg2Br2 crystals, the large anisotropic mechanical and thermal properties could be explained, which are mainly attributed to the one-dimensional chain structure of the compound. Notably, the mechanical and thermal properties of Hg2Br2 crystals at low temperature are better than those at high temperature, which guarantees the practical application of AOTFs in a space extreme environment.

chemistry, multidisciplinary,materials science,crystallography