Controlled growth of perovskite layers with volatile alkylammonium chlorides

Jaewang Park,Jongbeom Kim,Hyun-Sung Yun,Min Jae Paik,Eunseo Noh,Hyun Jung Mun,Min Gyu Kim,Tae Joo Shin,Sang Il Seok

DOI: https://doi.org/10.1038/s41586-023-05825-y

IF: 64.8

2023-02-17

Nature

Abstract:Controlling the crystallinity and surface morphology of the perovskite layers by methods such as solvent engineering 1,2 and methylammonium chloride addition 3-7 is an effective strategy for achieving high-efficiency perovskite solar cells (PSCs). In particular, it is essential to deposit an α-formamidinium lead iodide (FAPbI 3 ) perovskite thin films with fewer defects due to their excellent crystallinity and large grain size. Herein, we report the controlled crystallisation of perovskite thin films with the combination of alkylammonium chlorides (RACl) added to FAPbI 3 . The δ- to α-phase transition of FAPbI 3 and the crystallisation process and surface morphology of the perovskite thin films coated with RACl under various conditions were investigated through in situ grazing incident wide-angle X-ray diffraction and scanning electron microscopy. RACl added to the precursor solution was believed to be easily volatilised during coating and annealing owing to dissociation into RA 0 and HCl with deprotonation of RA + induced by RA···H + -Cl - binding to PbI 2 in FAPbI 3 . Thus, the type and amount of RACl determined the δ- to α-phase transition rate, crystallinity, preferred orientation, and surface morphology of the final α-FAPbI 3 . The resulting perovskite thin layers facilitated the fabrication of PSCs with a power conversion efficiency of 26.08% (certified 25.73%) under standard illumination.

multidisciplinary sciences