Electrospun Modified Polyketone-Based Anion Exchange Membranes with High Ionic Conductivity and Robust Mechanical Properties

Yi-cun Zhou,Rui-Ying Bao,Zhengying Liu,Ming-Bo Yang,Wei Yang

DOI: https://doi.org/10.1021/acsaem.1c00727

IF: 6.4

2021-05-03

ACS Applied Energy Materials

Abstract:It is still a significant challenge to rationally design and delicately process or fabricate anion exchange membranes (AEMs) with high ionic conductivity, good mechanical properties, and sufficient alkaline stability. Here, a polyketone (PK) resin-based AEM was synthesized via the Paal–Knorr reaction and quaternary ammonium reaction, and then processed by electrospinning and hot pressing technologies. In contrast to a quaternized functional polyketone-based polyelectrolyte (QAFPK) fabricated by casting, the electrospun QAFPK shows higher hydroxide conductivity and robust mechanical properties. QAFPK-1-6-E realizes a hydroxide conductivity of 181 mS/cm at 80 °C and a tensile strength of 54 MPa. The microphase structure characterization indicates that the electrospinning process can induce the formation of an excellent ion-conducting structure. The electrospun PK-based AEM displays great application potential in a variety of electrochemical devices under alkaline conditions, such as alkaline anion exchange membrane fuel cells (AAEMFCs).The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c00727?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c00727</a>.Schematic diagram of the ion conductivity test device; additional SEM surface images of QAFPK-1-<i>n</i>-E (<i>n</i> = 8, 6 and 5) before and after hot pressing; additional SEM cross-section images of QAFPK-1-<i>n</i>-C and QAFPK-1-<i>n</i>-E (<i>n</i> = 8, 6 and 5); additional AFM height images of QAFPK-1-<i>n</i>-C and QAFPK-1-<i>n</i>-E (<i>n</i> = 8, 6 and 5); histogram of average ion cluster size calculated by SAXS; stress versus strain curves and mechanical properties of QAFPK-1-<i>n</i>-E (<i>n</i> = 8, 6 and 5) perpendicular to the direction of fiber orientation; apparent activation energy (<i>E</i>_a) of the OH^– and CI^– transport of the membranes; and supplementary comparison of the properties of electrospun polyketone-based AEMs having QA cation and other literature works (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c00727/suppl_file/ae1c00727_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,chemistry, physical,energy & fuels