Abstract:Highlights • Three cumene hydroperoxide derivatives were synthesized. • Self-cure composites based on various hydroperoxides were formulated and evaluated. • Excellent mechanical properties were obtained with the new hydroperoxides. • The nature of the hydroperoxide had a strong influence on the curing kinetics. Objectives Hydroperoxides are key constituents of two-component dental materials. The objective of this study was to evaluate the influence of the hydroperoxide structure on the reactivity and on the mechanical properties of self-cure composites. Methods Hydroperoxides HP1–3 were synthesized by selective catalytic oxidation of the corresponding para -substituted cumene precursors and isolated in high purity. They were characterized by 1 H NMR and 13 C NMR spectroscopy. 16 self-cure composites, based on the redox initiator system hydroperoxide (Cumene hydroperoxide (CHP), HP1–3 or tert .-Amyl hydroperoxide (TAH))/polymerizable thiourea ATU1 /copper(II) acetylacetonate, were formulated in Sulzer Mixpac two-component syringes. An equimolar hydroperoxide/ ATU1 ratio was selected for each self-cure composite. The reactivity and the final double-bond conversions obtained with these two-component materials was assessed using RT-FTIR spectroscopy. The flexural strength and modulus were measured using a three-point bending setup, after storage of the specimens for 45 min at 37 °C (dry) and for 24 h in water at 37 °C. The working time of each self-cure composite was measured using an oscillating rheometer. Results CHP derivatives bearing an electron withdrawing group ( HP2 : ester or HP3 : nitrile) in the para position were found to be more reactive than CHP, whereas the compound bearing an electron donating group ( tert -butyl, HP1 ) was less reactive; molecular modelling data were reported for a better understanding of this structure/reactivity/efficiency relationship. All CHP derivatives were more reactive than the aliphatic hydroperoxide TAH. Excellent mechanical properties were obtained with self-cure composites containing either CHP or a para -functionalized CHP derivative. By carefully selecting the amounts of oxidizing/reducing agents and metal catalyst, suitable working times can be obtained with all evaluated hydroperoxides. HP3 , thanks to its high reactivity, is nonetheless the most promising compound. Significance The curing rate of self-cure composites can be adapted by modifying the structure of the hydroperoxide. In agreement with molecular modelling data, the incorporation of CHP derivatives bearing an electron withdrawing group in the para position is particularly attractive. Indeed, due to a significant reactivity enhancement, the desired properties (working time, flexural strength/modulus) can be obtained by incorporating moderate amounts of hydroperoxide/acylthiourea as well as particularly low contents of metal catalyst to the two-component dental materials.

Lignin-derived new hydrogen donors for photoinitiating systems in dental materials

Novel lignin α-O-4 derived hydrogen donors in CQ-based photoinitiating systems for dental resins

Low‐Migration Compounds with Amine Functionality as Co‐Initiators of Radical Polymerization

Effect of proanthocyanidins and photo-initiators on photo-polymerization of a dental adhesive

Evaluation of the Selected Mechanical and Aesthetic Properties of Experimental Resin Dental Composites Containing 1-phenyl-1,2 Propanedione or Phenylbis(2,4,6-trimethylbenzoyl)-phosphine Oxide as a Photoinitiator

A hydroxyl-containing hyperbranched polymer as a multi-purpose modifier for a dental epoxy

Color stability, conversion, water sorption and solubility of dental composites formulated with different photoinitiator systems

Bio-based epoxy resins derived from diphenolic acid via amidation showing enhanced performance and unexpected autocatalytic effect on curing

The Photoinitiators Used in Resin Based Dental Composite—A Review and Future Perspectives

Moving Towards a Finer Way of Light-Cured Resin-Based Restorative Dental Materials: Recent Advances in Photoinitiating Systems Based on Iodonium Salts

Flexural strength of dental adhesives with different photoinitiator systems

Layered double hydroxides intercalated with fluoride and methacrylate anions as multifunctional filler of acrylic resins for dental composites

Synthesis and characterization of dimethacrylates containing quaternary ammonium functionalities for dental applications

Preparation and Properties of Novel Dentin Adhesives with Esterase Resistance

Effects on dentin nanomechanical properties, cell viability and dentin wettability of a novel plant-derived biomodification monomer

Highly Efficient Photoinitiation Systems Based on Dibenzo[a,c]phenazine Sensitivity to Visible Light for Dentistry

Light-Cured Self-Etch Adhesives Undergo Hydroxyapatite-Triggered Self-Cure

Enhancing resin-dentin bond durability using a novel mussel-inspired monomer

Influence of the hydroperoxide structure on the reactivity and mechanical properties of self-cure dental composites

Light-curable urushiol enhanced bisphenol A glycidyl dimethacrylate dentin bonding agent

Restorative Dental Resin Functionalized with Calcium Methacrylate with a Hydroxyapatite Remineralization Capacity