Temperature dependence of the shock-induced reversal of martensite to austenite in an iron-nickel-carbon alloy

R.W Rohde

DOI: https://doi.org/10.1016/0001-6160(70)90018-0

1970-08-01

Acta Metallurgica

Abstract:Shock compression experiments have been used to measure the temperature dependence from 25 to 390°C of the transition pressure associated with the reversal of martensite to austenite in an Fe-28.4 at. % Ni-0.5 at. % C alloy. The transition pressure decreases nonlinearly from 67 kbar at 45°C to about 6 kbar at 390°C. Above 300°C the slope of the phase line is −0.25 kbar/°C, whereas below 250°C the slope is − 0.14 kbar/°C. These data are analyzed by two thermodynamic procedures; 1.(i) by assuming the reversal is an isothermal transformation, and2.(ii) by assuming that the reversal is an adiabatic transformation. The latter procedure provides the better fit to the data. Previous hydrostatic pressure measurements of the transition from 300° to 380°C are compared with the shock compression data. Although the temperature coefficients determined in the two separate experiments are the same, the transition pressure determined in the hydrostatic experiments is about 10 kbar lower than the transition pressure determined in the shock experiments. This discrepancy is caused by a partial reversal of martensite due to the presence of shear stresses in the shock compression experiments.