Abstract:Cu and unoxidized graphene composite films were prepared by electroplating under room temperature. Graphene was added to the electrolyte of Cu to form composite materials to improve the performance of Cu for interconnection. Composite electrolyte containing high concentration of graphene (up to 0.5 g/L) was prepared by adding CTAB as surfactant. And ultrasound was also used to increase dispersion degree and reduce graphene agglomeration in electrolyte. Average coefficient of thermal expansion (CTE) of the composite films determined by thermo-mechanical analysis (TMA) shows a decrease from 17.3 ppm/K to 14.2 ppm/K from 260 K to 320 K, which reduce CTE by 18 % compared with Cu. CTE of the composite materials can be reduced to 10 ppm/K at 243 K, which is only 60 % of CTE of Cu. The thermal conductivity of the composite materials measured by phase sensitive transient thermo-reflectance (PSTTR) technique shows an improvement from 385 W/m.K to 468 W/m.K. CTE and thermal conductivity of the composite materials both decrease with the increase of current density. And they also both increase with the increase of graphene concentration. The composite materials also show good mechanical properties. The average hardness is 2.5 GPa, which is about 2 times of Cu. And the average elastic modulus is 145 GPa, which is 38 % higher than that of Cu. The resistivity of the composite materials is basically equivalent to that of pure Cu. Result of the experiment proved that the composite materials have better performance under low temperature conditions. The improvement of material properties makes composite materials have good application prospects for 3D interconnection in the near future.

Strong Enhancement of Thermal Properties of Copper Films after Chemical Vapor Deposition of Graphene

Temperature Coefficient of Resistance in Graphene-Coated Cu from First Principles

First Principles Calculation of Effect of Graphene Coating on Transmission Coefficient of Cu Thin Film with Low Surface Roughness

An Investigation of Electric Resistance of Graphene-Coated Copper Thin Film from First Principles

Effects Of Thermally-Induced Changes Of Cu Grains On Domain Structure And Electrical Performance Of Cvd-Grown Graphene

Enhanced Electrical Conductivity and Tensile Strength of Cu/Single-Layer Graphene/Cu Nanomaterials

Enhanced Heat Dissipation for Macroscopic Metals Achieved by a Single-Layer Graphene

Enhanced the thermal conductivity of flexible copper foil by introducing graphene

Enhancement of Thermal Management Performance of Copper Foil Using Additive–Free Graphene Coating

Synthesis and characterization of graphene on copper foil via atmospheric pressure chemical vapor deposition method and its impact on electrical properties

Fabrication and Thermal Conductivity of Copper Coated Graphite Film/aluminum Composites for Effective Thermal Management

Enhanced room-temperature corrosion of copper in the presence of graphene.

Surface morphology and associated high temperature evolution of copper covered with vapor deposited graphene

The Influence of Graphene Substrate on Microstructures and Electrical Properties of Vapor-Deposited Copper Thin Films

A modified spin-casting approach for scalable preparation of ultra-thick reduced graphene oxide films with high thermal conductivity

Chemical Vapour Deposition of Graphene for Durable Anticorrosive Coating on Copper

Chemical Vapor Deposition of Graphene on Thin-Metal Films

Significant enhancement of metal heat dissipation from mechanically exfoliated graphene nanosheets through thermal radiation effect

Preparation and Characterization of Electroplated Cu/Graphene Composite

Effect of graphene on thermal and mechanical properties of copper-titanium carbide composites

Thermal and Electrical Conductivity of Copper‐Graphene Heterosystem: An Effect of Strain and Thickness