Study on Mechanism of Microstructure Evolution Induced by Grinding for Single Crystal Superalloy
XU Yun-chao,LI Jing-dong,ZHANG Zhi-xin,PANG Gui-bing,GONG Ya-dong
DOI: https://doi.org/10.16490/j.cnki.issn.1001-3660.2023.12.007
2023-01-01
Surface Technology
Abstract:Due to its excellent creep and fatigue resistance at high temperatures,the microstructure control during the forming and mechanical processing of single crystal superalloy widely used in hot end components of aircraft engines has always been a hot topic of concern.At present,the theory of dislocation slip and recrystallization at high strain rates for this special material without original grain boundaries is currently unclear.Thus,the mechanism of microstructure evolution on the surface of single crystal superalloy parts was obtained through grinding experiments in this work.The sample for transmission electron microscopy(TEM)of ground surface was prepared by focused ion beam(FIB)directed cutting technique.The microstructure,orientation,grain size,and dislocation density distribution on the ground surface were characterized using field emission scanning electron microscopy(FE-SEM),X-ray diffraction technology(XRD),TEM,and transmission Kikuchi diffraction(TKD)technology,respectively.The results indicate that a gradient structure with white layer,plastic deformation layer,and bulk material are formed below the ground surface,and dynamic recrystallization phenomenon is generated on the subsurface.The SEM results show that there is no obvious deformation feature in the white layer,while a large number of slip traces are formed in the plastic deformation layer.The original structure of γ/γ′ phase is destroyed,exhibiting typical shear deformation characteristics.XRD results show that the original single orientation of the single crystal superalloy is transformed into multiple diffraction peaks(111),(200),(220),(311)and(222).TEM detection indicate that dynamic recrystallization occurred in the top surface layer of single crystal parts during grinding,resulting in grain refinement at the nanoscale.The surface of single crystal parts has transformed from a special organizational structure with only a single grain to a polycrystalline structure characterized by the coexistence of nano equiaxed grains and subgrains.A large number of high-density dislocation structures are formed on the subsurface.TKD results show that under the high-speed rotation and shear action of the grinding wheel,plastic deformation are generated on the ground surface along the shear direction,and the original Cube texture transformed into R-Cube texture and F texture.Grains with{111}<112>,{001}<110>,and{001}<100>orientations were formed along the grinding depth direction,respectively.The evolution of microstructure orientation caused by shear strain during grinding indicates that the recrystallized grains and deformed microstructure are generated by lattice rotation,driving the{111}plane parallel to the shear plane,while the<110>direction is consistent with the shear direction.Moreover,the high-density crystal defects formed during plastic deformation can adapt to strain,leading the crystal direction to develop towards the direction with the highest shear stress.This lattice rotation method can provide a macroscopic direction that is easy to shear for grinding,resulting in a smaller grinding force during the grinding process and facilitating material removal.The microstructure changes on the ground surface of single crystal superalloy are the evolution mechanism of dynamic recrystallization dominated by lattice rotation and dislocation slip motion.The research on the microstructure during the grinding process of single crystal parts has improved the recrystallization theory of single crystal materials,providing experimental and theoretical basis for controlling orientation changes in actual machining of single crystal blades.