Effect of Sn on stacking fault energies in zirconium and its hydrides

P. Chakraborty,I. Mouton,B. Gault,A. Tehranchi,J. Neugebauer,T. Hickel

DOI: https://doi.org/10.1103/physrevmaterials.8.033605

IF: 3.98

2024-03-19

Physical Review Materials

Abstract:Hydrogen embrittlement in Zr-alloy fuel cladding is a primary safety concern for water-based nuclear reactors. Here we investigated the stabilization of planar defects within the forming hydrides by Sn, the primary alloying element of Zircaloy-4 used in the cladding. In order to explain the formation of hydrides and planar defects observed in our experiments, we performed atomic-scale ab initio calculations focusing on the solute interactions with generalized stacking faults in hcp α -Zr and fcc zirconium hydrides. Our calculations showed that an increase in Sn concentration leads to a stabilization of stacking faults in both the α -Zr and hydride phases. However, the solution enthalpy of Sn is lower in the α -Zr as compared to the other hydride phases, indicative of two competing processes of Sn depletion/enrichment at the Zr hydride/matrix interface. This is corroborated by experimental findings, where Sn is less soluble in hydrides and is mostly found trapped at interfaces and planar defects, indicative of stacking faults inside the hydride phases. Our systematic investigation enables us to understand the presence and distribution of solutes in the hydride phases, which provides a deeper insight into the microstructural evolution of such alloy's properties during its service lifetime. https://doi.org/10.1103/PhysRevMaterials.8.033605 Published by the American Physical Society under the terms of the Creative Commons Attribution 4.0 International license. Further distribution of this work must maintain attribution to the author(s) and the published article's title, journal citation, and DOI. Open access publication funded by the Max Planck Society. Published by the American Physical Society

materials science, multidisciplinary

What problem does this paper attempt to address?

The paper aims to address the issue of hydrogen embrittlement in zirconium alloy cladding materials during nuclear reactor operation, particularly focusing on the effect of tin (Sn) on the stacking fault energies (SFE) of zirconium and its hydrides.

Specifically, the paper investigates the following aspects:
1. **Experimental Background**: Zirconium-based alloys are widely used as nuclear reactor fuel cladding materials due to their low thermal neutron absorption cross-section and good corrosion resistance. However, during operation, contact between zirconium and water leads to oxidation, which releases hydrogen gas. Some of the hydrogen enters the alloy and exceeds the solubility limit, forming brittle hydrides that affect the material's integrity and lifespan.
2. **Research Methods**: Using first-principles calculations at the atomic scale, the study focuses on the interaction of tin with the generalized stacking faults (GSF) in hexagonal close-packed (hcp) α-Zr phase and face-centered cubic (fcc) zirconium hydrides.
3. **Main Findings**: Increasing tin concentration can stabilize the stacking fault structures in both α-Zr and hydride phases. However, the enthalpy of solution of tin in α-Zr is lower than in other hydride phases, indicating two competing processes: depletion/enrichment of tin at the zirconium hydride/matrix interface. Experimental results also confirm this, showing that the solubility of tin in hydrides is low and that tin is mainly trapped at interfaces and planar defects.
4. **Combination of Theory and Experiment**: By systematically studying the distribution of Sn in different phases, the paper reveals the presence and distribution of solutes in the hydride phase, providing deep insights into the microstructural evolution of such alloys during service.

In summary, through theoretical calculations and experimental validation, the paper explores how tin affects the stacking fault energies of zirconium alloys and their hydrides, thereby providing a theoretical basis for addressing the hydrogen embrittlement issue in zirconium alloy cladding materials in nuclear reactors.