Study of the Rolling Effect on MoS2–Carbon Fiber Density and Its Consequences for the Functionality of Li-Ion Batteries

Tai-Yu Wu,Xiao-Ru Li,Bo-Chun Chen,Li-Wen Wang,Jia-Hao Wang,Sheng-Yuan Chu,Chia-Chin Chang

DOI: https://doi.org/10.3390/ma17122825

IF: 3.4

2024-06-11

Materials

Abstract:In this study, an electrode slurry composed of molybdenum disulfide (MoS2) and vapor-grown carbon fiber (VGCF) prepared through a solid-phase synthesis method was blade-coated onto copper foil to form a thick film as the anode for lithium-ion batteries. In previously reported work, MoS2-based lithium-ion batteries have experienced gradual deformation, fracture, and pulverization of electrode materials during the charge and discharge cycling process. This leads to an unstable electrode structure and rapid decline in battery capacity. Furthermore, MoS2 nanosheets tend to aggregate over charge and discharge cycles, which diminishes the surface activity of the material and results in poor electrochemical performance. In this study, we altered the density of the MoS2–carbon fiber/Cu foil anode electrode by rolling. Three different densities of electrode sheets were obtained through varying rolling repetitions. Our study shows the best electrochemical performance was achieved at a material density of 2.2 g/cm3, maintaining a capacity of 427 mAh/g even after 80 cycles.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper aims to address the issues encountered with molybdenum disulfide (MoS₂)-based anode materials in lithium-ion batteries during charge-discharge cycles, including gradual deformation, cracking, and pulverization of the material, leading to unstable electrode structures and rapid capacity decline. Additionally, MoS₂ nanosheets tend to aggregate during charge-discharge processes, which reduces the surface activity of the material and thus affects its electrochemical performance.

To solve these problems, researchers improved the electrochemical performance of MoS₂ by altering the density of MoS₂ and carbon fiber composites. Specifically, they obtained electrode sheets with different densities through varying the number of rolling passes and found that when the material density was 2.2 g/cm³, the electrode exhibited optimal electrochemical performance, maintaining a capacity of 427 mAh/g even after 80 cycles. This study provides a new approach to enhancing the stability and cycle life of MoS₂-based lithium-ion batteries.