Boosted lithium storage performance by local build-in electric field derived by oxygen vacancies in 3D holey N-doped carbon structure decorated with molybdenum dioxide
Chuanxin Hou,Wenyue Yang,Hideo Kimura,Xiubo Xie,Xiaoyu Zhang,Xueqin Sun,Zhipeng Yu,Xiaoyang Yang,Yuping Zhang,Bin Wang,Ben Bin Xu,Deepak Sridhar,Hassan Algadi,Zhanhu Guo,Wei Du
DOI: https://doi.org/10.1016/j.jmst.2022.10.007
IF: 10.319
2022-11-14
Journal of Materials Science and Technology
Abstract:Highlights • 3D porous N-doped carbon decorated with MoO 2 nanoparticles were synthesized; • Oxygen vacancies were introduced into the prepared composites; • The differential charge density distribution and density of states were applied; • A 918.2 mAh g −1 at 0.1 A g −1 after 130 cycles were obtained for Li storage; • The kinetic analysis of MoO 2 /C electrodes for Li storage was carried out. Three-dimensional holey nitrogen-doped carbon matrixes decorated with molybdenum dioxide (MoO 2 ) nanoparticles have been successfully synthesized via a NaCl-assisted template strategy. The obtained MoO 2 /C composites offered multi-advantages, including higher specific surface area, more active sites, more ions/electrons transmission channels, and shorter transmission path due to the synergistic effect of the uniformly distributed MoO 2 nanoparticles and porous carbon structure. Especially, the oxygen vacancies were introduced into the prepared composites and enhanced the Li + intercalation/deintercalation process during electrochemical cycling by the Coulomb force. The existence of the local built-in electric field was proved by experimental data, differential charge density distribution, and density of states calculation. The uniquely designed structure and introduced oxygen vacancy defects endowed the MoO 2 /C composites with excellent electrochemical properties. In view of the synergistic effect of the uniquely designed morphology and introduced oxygen vacancy defects, the MoO 2 /C composites exhibited superior electrochemical performance of a high capacity of 918.2 mAh g –1 at 0.1 A g –1 after 130 cycles, 562.1 mAh g –1 at 1.0 A g –1 after 1000 cycles, and a capacity of 181.25 mAh g –1 even at 20.0 A g –1 . This strategy highlights the path to promote the commercial application of MoO 2 -based and other transition metal oxide electrodes for energy storage devices.
materials science, multidisciplinary,metallurgy & metallurgical engineering