Effect of grain boundary reconstruction and regenerated main phase shell on magnetic properties in high-abundance (NdLaCeY)-Fe-B magnets
Zhi Jia,Mingpeng Kou,Yuhao Li,Shuai Cao,Guangfei Ding,Shuai Guo,Xiaodong Fan,Chaoqun Zhu,Renjie Chen,Aru Yan
DOI: https://doi.org/10.1016/j.jmrt.2023.04.110
IF: 6.267
2023-04-24
Journal of Materials Research and Technology
Abstract:The (NdLaCeY)-Fe-B magnets with 45–50 wt% high-abundance rare earth substitution were systematically investigated by co-mixing high boron content matrix phase and Pr–Fe alloy powders (0, 1, 3, 5, 7, and 9 wt%) during the preparation process. The coercivity of magnets increased successively with the addition of Pr 70 Fe 30 (wt.%) and reached 9.32 kOe at the addition amount of 9 wt% from the initial 7.33 kOe without addition, while the remanence had a very small decrease of only 0.13 kGs. The analyses showed that the B-rich phase in the high-boron powders reacted with Pr 70 Fe 30 to form the main phase shell, forming a core-shell structure with a Pr-rich shell and a Y-rich core. Meanwhile, the grain boundary was significantly widened with the introduction of Pr 70 Fe 30 . Then, just the improved anisotropy of the main phase grain surface, accompanied with the enhanced magnetic de-coupling effect between the main phase grains, resulted in a great coercivity increment. Notably, on the remanence, the beneficial effect of increased main-phase proportion by regenerated grain shell had a competitive relationship with the deteriorating effect of the magnetic dilution by the non-magnetic material introduction, thus under the combined effects, the remanence firstly increased and then decreased with the addition of Pr–Fe.
materials science, multidisciplinary,metallurgy & metallurgical engineering