Abstract:A homogeneous alpha-Al2O3 crystal membrane was fabricated by the sol-gel technique on 316L porous stainless steel (PSS) substrate with an average pore size of 1.0 mu m. The preparation process was optimized by carefully choosing the binder, the concentrations of the casting solutions and the sintering temperatures of the membranes. Compared to methylcellulose and polyethylene glycol 20000, polyvinyl alcohol 1750 was found to be the most effective binder to fabricate a homogeneously structured Al2O3 membrane without defects. The concentration to prepare an uniform coverage membrane with a thickness of similar to 10 mu m was 0.032 mol/L. When sintered at 1000 A degrees C, gamma-Al2O3 membrane with similar to 3 mu m grains was obtained. When sintered at 1200 A degrees C, gamma-Al2O3 completely transformed into alpha-Al2O3 and the grains grew to similar to 5 mu m. Accordingly, the process was applied to a bigger pore-sized PSS with an average pore size of 1.5 mu m to fabricate an alpha-Al2O3 intermediate layer to initially modify its surface. A single alpha-Al2O3 crystal layer with a thickness of similar to 5 mu m and an average pore size of 0.7 mu m was achieved. Subsequently, TiO2, SiO2, and TiO2-SiO2 hybrid membranes were tried on the modified PSS. Defect-free microfiltration membranes with average pore sizes of similar to 0.3 mu m were readily fabricated. The results indicate that the sol-gel method is promising to initially modify the PSS substrates and the sol-gel-derived alpha-Al2O3 crystal layer is an appropriate intermediate layer to modify the PSS and to support smaller grain-sized top membranes.

Fabrication of novel porous Al2O3 substrates by combining emulsion templating and gel-tape-casting methods

Novel Fabrication Processing of Porous Al2O3/CaAl12O19 Membrane by Combining Emulsion, Cement Curing and Tape-Casting Methods

Effect of Type and Content of Pore-forming Agents on Properties of Porous Alumina Membrane Support

Fabrication of Nanoporous Alumina Ultrafiltration Membrane with Tunable Pore Size Using Block Copolymer Templates

Zeolite Imidazolate Framework Membranes on Polymeric Substrates Modified with Poly(vinyl Alcohol) and Alginate Composite Hydrogels.

A Simple Method for Fabrication of Highly Ordered Porous Alpha-Alumina Ceramic Membranes

Flexible Fabrication of New-Type Porous Anodic Alumina Membranes with Tunable Geometric Features by Low-Cost Nanoimprint Lithography.

Melded Ceramic Membranes: A Novel Fabrication Method for Ultrathin Alumina Membranes of High Performance

Facile fabrication of surfactant-templated silica membrane on porous alumina support

Superspreading‐Based Fabrication of Asymmetric Porous PAA‐g‐PVDF Membranes for Efficient Water Flow Gating

Asymmetric alumina-based ultrathin composite ceramic membranes with interfacial modification of black talc nanosheets

A Sol–gel-Derived Α-Al2o3 Crystal Interlayer Modified 316L Porous Stainless Steel to Support TiO2, SiO2, and TiO2–SiO2 Hybrid Membranes

Synthesis of Microporous Membranes and Films on Various Substrates by Novel Electrospinning Method

One-step fabrication of asymmetric alumina ceramic membranes with tunable pore parameters for oil-water separation

Facile Fabrication of Reinforced Homoporous MF Membranes by in Situ Breath Figure and Thermal Adhesion Method on Substrates

Preparation and Gas Permeation of Supported Γ-Al2o3 Membranes Used As Substrate Layer for Microporous Membranes

Fabrication of Transferable Perforated Isoporous Membranes on Versatile Solid Substrates Via the Breath Figure Method

A sol–gel-derived α-Al 2 O 3 crystal interlayer modified 316L porous stainless steel to support TiO 2 , SiO 2 , and TiO 2 –SiO 2 hybrid membranes

Integrated preparation of alumina microfiltration membrane with super permeability and high selectivity

Environmental Friendly Fabrication of Porous Cement Membranes Via Reusable Camphene-Based Freeze-Casting Method

Fabrication of three-dimensional superhydrophobic membranes with high porosity via simultaneous electrospraying and electrospinning