Highly Transparent, Robust Hydrophobic, and Amphiphilic Organic–Inorganic Hybrid Coatings for Antifogging and Antibacterial Applications
Yubin Jeon,Saravanan Nagappan,Xi-Hui Li,Joon-Hee Lee,Liyi Shi,Shuai Yuan,Won-Ki Lee,Chang-Sik Ha
DOI: https://doi.org/10.1021/acsami.0c20401
2021-01-28
Abstract:The control of surface wettability through a combination of surface roughness, chemical composition, and structural modification has attracted significant attention for antifogging and antibacterial applications. Herein, a two-step spin-coating method for amphiphilic organic–inorganic hybrid materials with incorporated transition metal ions is presented. The coating solution was prepared via photochemical thiol–ene click reaction between the mercapto functional group in trimethylolpropane tris(3-mercaptopropionate) and the vinyl functionalized silica precursor 3-(trimethoxysilyl)propyl methacrylate. In the first step of coating, a glass substrate was coated using a solution of metal nitrate hydrates and subsequently showed hydrophobic properties. As the second step, the spin-coated glass substrate was further coated with silica nanoparticles (SiO<sub>2</sub> NPs) and polycaprolactone triol (PCT) suspension, where the contents of SiO<sub>2</sub> NPs were fixed at 0.1 wt %, unless otherwise noted. The coated substrate exhibited hydrophilic properties. For comparison, the coating was also formulated with the SiO<sub>2</sub> NPs/PCT suspension without SiO<sub>2</sub> NPs and with 0.5 wt % SiO<sub>2</sub> NPs as well as by adjusting different coating layer thicknesses. The surface morphology and chemical compositions of the obtained coating materials were analyzed by field emission scanning electron microscopy with energy-dispersive X-ray spectroscopy and X-ray photoelectron spectroscopy. The transparency and static contact angle of coated samples were measured by UV–visible spectrophotometry and drop shape analysis, respectively. It was concluded that our novel hybrid coating materials exhibited excellent antibacterial and antifogging properties with extremely high scratch resistance and transparency.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c20401?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c20401</a>.Scheme for the coating fabrication procedure using a layer-by-layer assembly (LBL) technique; optical images of MFM solutions with or without metal sources regarding to the stability; <sup>29</sup>Si NMR spectrum of ZnFM-AE; EDS graphs and mapping of each elemental composition for substrates of ZnFM-E, ZnFM-E-PSi 0.1, and AlFM-E-PSi 0.1; FESEM images of PSi 0.5-modified XFM-E and XFM-AE; AFM images of MFM-E, ZnFM-E, ZnFM-E-PSi 0.1, XFM-E-PSi 0.1, and XFM-AE-PSi 0.1; optical images of water and hexadecane (oil) contact angles; UV–visible transmittance, antifogging, and antibacterial properties of the samples; stability of the coated substrates under harsh conditions; tables for the description of the bacterial medium, atomic percentage values of samples identified by EDS graphs, and AFM roughness values; comparison of various approaches for developing antifogging and antibacterial coatings (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c20401/suppl_file/am0c20401_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology