Abstract:α-hemihydrate (α-HH), known for its exceptional mechanical properties, is a widely used building material. Despite its advantages, the traditional method of producing α-HH through regular pressure brine poses significant drawbacks. These include substantial industrial salt demands, high production costs, and water pollution. A more environmentally friendly α-HH preparation process has been developed to counteract these issues, combining FGD gypsum and concentrated brine. This study delves into the effects of the principal ions present in concentrated brine on the phase transition process and the microstructure of the final product. Our findings reveal that the reaction rate accelerates with increased concentrations of Ca2+, Mg2+, K+, and Na+ in concentrated brine. However, excessive Na+ concentration can alter the phase transition process, converting the product to β-HH. Additionally, an overly high concentration of KCl may prompt a part of the K+ to engage in the reaction, leading to the formation of isomeric potassium gypsum. This process can disrupt the original structure of hemihydrate gypsum. The addition of maleic acid to the salt solution was found to foster anhydrous gypsum formation. In contrast, succinic acid can decrease the crystals' aspect ratio, resulting in the growth of short columns, thereby enhancing the product's strength performance. Our research also identified that the reaction rate elevates as the pH value declines. However, an acidic environment diminishes the size of the crystal and counteracts the crystal modifier's effects. Lastly, incorporating CaCl2 and MgCl2 into concentrated brine with a low Na+ concentration can convert FGD gypsum into high-strength α-HH. This transformation results in a product boasting a 1-day compressive strength of 40.5 MPa.

Microstructure and mechanical properties of β-hemihydrate produced gypsum: An insight from its hydration process

Hydration characteristics and mechanism analysis of β-calcium sulfate hemihydrate

Effect of borax on the hydration and hardening of β-hemihydrate gypsum at high water–plaster ratio

Effect of Particle Size Distribution on the Hydration and Compressive Strength Development of Α-Calcium Sulfate Hemihydrate Paste

Trace NaCl and Na2EDTA Mediated Synthesis of Α-Calcium Sulfate Hemihydrate in Glycerol–Water Solution

Hydration Mechanism and Hardening Property of α-Hemihydrate Phosphogypsum

Insights Into the Micromechanics of Dehydration‐Induced Gypsum to γ‐Anhydrite Phase Transition From Instrumented Microindentation Experiments

Experimental Study on Physical and Mechanical Properties of Gypsum Rock During High-Temperature Dehydration–Hydration Expansion

Study on physical and chemical characteristics of β-hemihydrate phosphogypsum

Impact of carboxylic acid structure on α-hemihydrate gypsum crystal morphology and mechanical strength

Coordinated disposal of FGD gypsum and power plant concentrated brine via preparation of α-hemihydrate gypsum

Formation of α-Hemihydrate Inside of a Gypsum Crystal during the Dehydration Process

Effect of Soluble Phosphorus on the Mechanical Properties of α-Hemihydrate Gypsum

Hydration reaction and microstructural characteristics of hemihydrate phosphogypsum with variable pH

Effect of modifiers on crystalizing habit and mechanical strength of α-hemihydrate gypsum prepared from PG by an autoclaved method

Preparation of Medium–Low Strength Hemihydrate Gypsum from Phosphogypsum and Grey Correlation Evaluation of Autoclaving Energy Consumption

Enhancing the hydration reactivity of hemi-hydrate phosphogypsum through a morphology-controlled preparation technology