Evaluation of Chitosan-Oleuropein Nanoparticles on the Durability of Dentin Bonding
Shuya Zhao,Yunyang Zhang,Yun Chen,Xianghui Xing,Yu Wang,Guofeng Wu
DOI: https://doi.org/10.2147/DDDT.S390039
2023-01-22
Abstract:Shuya Zhao, 1 Yunyang Zhang, 2 Yun Chen, 3 Xianghui Xing, 1 Yu Wang, 1 Guofeng Wu 4 1 Department of Pediatric Dentistry, Nanjing Stomatological Hospital, Medical School of Nanjing University, Nanjing, People's Republic of China; 2 Center of Modem Analysis, Nanjing University, Nanjing, People's Republic of China; 3 Department of Pediatric Dentistry, Affiliated Hospital of Stomatology, Nanjing Medical University, Nanjing, People's Republic of China; 4 Department of Prosthodontics, Nanjing Stomatological Hospital, Medical School of Nanjing University, Nanjing, People's Republic of China Correspondence: Guofeng Wu; Xianghui Xing, Email ; Purpose: To evaluate the effects of dentin pretreatment with chitosan-loaded oleuropein nanoparticles (CONPs) on the durability of resin–dentin bonding interfaces. Methods: Eighty freshly extracted non-carious human third molars were randomly divided into four groups (n = 20 each): a de-ionized water (DW) group, a chitosan (CS) group, a chlorhexidine (CHX) group and a CONP group. The dentin in the DW, CS, CHX, and CONP groups were pretreated with de-ionized water, 1.0 mg/L CS solution, 2% chlorhexidine solution, and CONP suspension (prepared with 100 mg/L oleuropein), respectively, followed by the universal adhesive and resin composites. The bonded teeth of each group were randomly divided into two subgroups: an immediate subgroup and an aged subgroup. The bonded teeth of each group were then cut into the bonded beams. We measured their microtensile bond strength (μTBS), observed the characteristics of bonding interface by atomic force microscope, calculated the percentage of silver particles in a selected area for interfacial nanoleakage analysis, and evaluated the endogenous gelatinase activity within the bonding interface for in-situ zymogram analysis. Data were analyzed with two-way ANOVA and LSD multiple comparison test ( P 0.05) in the CONP and CHX groups after 24 h. Besides, the CONP group presented significantly higher modulus of elasticity in the hybrid layers ( P < 0.05), lower expression of nanoleakage ( P < 0.05), and better inhibitory effect of matrix metalloproteinases than the other three groups before and after thermocycling. Conclusion: Altogether, the CONPs had the potential to act as a dentin primer, which could effectively improve the dentin-resin binding durability. Keywords: atomic force microscopy, dentin, matrix metalloproteinases, microtensile bond strength, nanoleakage Various factors, such as caries, abrasion, and trauma, can lead to the defect of teeth. Due to a lack of cellular components, teeth cannot self-repair. Clinically, composite resin materials for bonding and filling are currently the most frequent treatment approach for repairing enamel and dentin defects. Dentin is a complex tissue composed of minerals, water, and organic components such as collagen. Because of the structural characteristics of dentin itself, the bonding effect between dentin and composite resin is not as good as that of enamel. The long-term effect of resin dentin bonding is inadequate and eventually leads to complications such restorative detachment and secondary caries. 1–3 The stability and durability of the dentin bonding interface has always been an urgent problem to be solved in the field of adhesive dentistry. The hybrid layer has been considered as the main bonding and retention structure of dentin. 4 Meanwhile, it also remains the most vulnerable area of the adhesive-resin bond. 5 Dentin contains a variety of matrix metalloproteinases (MMPs) and cysteine cathepsins, which usually exist in the form of zymogen. When the tooth is stimulated by heat treatment, acid erosion, caries, and mechanical preparation, the zymogen will be activated to dissolve the dentin collagen matrix. 6 The unprotected collagen fibrils within the hybrid layer are susceptible to degradation and disintegration due to these activated enzymes. 7,8 Collagen degradation will lead to the loss of the anchoring function of the hybrid layer, with the consequent loss of bond strength. 9 Therefore, the application of protease inhibitors in the bonding process can prevent the degradation of collagen fibers and improve the durability of dentin resin bonding. 10,11 The use of synthetic MMP-inhibitors has been proposed to increase the durability of resin dentin bonds. 12,13 Among these different app -Abstract Truncated-
pharmacology & pharmacy,chemistry, medicinal