Effect of Traveling Speed on Microstructure and Stress Corrosion Cracking of ATZ511 Magnesium Alloy Friction Stir Welded Joints

Yulai Song,Weiguang Li,Linyang Zhang,Nan Wang,Boyang Liu

DOI: https://doi.org/10.1007/s11665-024-10047-y

IF: 2.3

2024-09-28

Journal of Materials Engineering and Performance

Abstract:The butt joints of the ATZ511 magnesium alloy plates were successfully prepared by using the friction stir welding method at different traveling speeds. The microstructure examination revealed that the size of the stir zone and shoulder-affected zone gradually reduced and the grain size of the stir zone gradually decreased in the process of traveling speed increased from 50 to 400 mm/min; however, the grain size of thermo-mechanical-affected zone became non-uniform at higher traveling speeds. The results of electrochemical experiments showed that the suitable traveling speed reduced the self-corrosion current of the welded joint, increased the transfer resistance, and improved the pitting resistance. Slow strain rate tensile tests showed that the stress sensitivity of welded joints was lowest when the traveling speed was 200 mm/min, and the stress sensitivity of tensile parts suddenly and significantly increased when the traveling speed reached 400 mm/min. The mechanism of improved stress corrosion resistance of welded joints lies in the fact that the appropriate traveling speed refines the microstructure and enhances the resistance to pitting corrosion.

materials science, multidisciplinary