Zn-Based Alloys for Plain Bearings—Influence of Al and Cu Content on Mechanical Properties

Angelika Kiefel,Steffen Gimmler,Christoph Broeckmann,Uwe Vroomen

DOI: https://doi.org/10.3390/ma17051062

IF: 3.4

2024-02-27

Materials

Abstract:In recent decades, the requirements for plain bearing materials have continually increased, especially with new applications such as wind turbines, which require larger bearings. These new applications have completely different property profiles compared with, for example, bearings in automotive construction. Larger bearings need high strength and wear resistance, which established bearing materials cannot fulfill. Therefore, new alloy systems are required. This publication focuses on the influence of alloy composition and test temperature on the mechanical properties of ZnAlCu alloys. Centrifugally cast specimens were produced for the fabrication of test specimens, which were used to determine the mechanical and tribological properties. Fracture surface and wear trace analysis with scanning electron and light microscopy were used to determine occurring failure and wear mechanisms and to analyze the influence of microstructure on failure. Depending on the composition of the ZnAlCu alloys, up to three times higher strengths can be achieved compared with the white metal alloy SnSb12Cu6ZnAg. Furthermore, all the alloys investigated show good wear properties. Up to 11 wt.% aluminum and 1.5 wt.% copper, a significant decrease in the wear coefficient was observed. Knowledge about the correlation between microstructure, properties, and failure mechanisms of ZnAlCu alloys can be used to produce bearing metal alloys suitable for a wide range of applications. Since the strength values lie between those of white metals and bronze, new fields of application can also be accessed.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem this paper attempts to address is: With the increasing demands on bearing materials from new applications such as wind turbines, existing bearing materials (such as white metal) are unable to meet the high strength and wear resistance required for these large bearings. Therefore, the paper investigates the mechanical and tribological properties of zinc-based alloys (ZnAlCu alloys) with varying aluminum and copper content and under different testing temperatures to evaluate their potential as new bearing materials.

Specifically, the paper addresses the problem through the following points:
1. **Effect of Alloy Composition**: Investigating the impact of different aluminum and copper content on the hardness, tensile strength, compressive strength, and wear resistance of ZnAlCu alloys.
2. **Effect of Testing Temperature**: Analyzing the effect of testing temperatures (room temperature and 100°C) on the mechanical properties of the alloys.
3. **Relationship Between Microstructure and Performance**: Using Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS) to analyze the microstructure of the alloys and explore its relationship with mechanical properties and wear mechanisms.

Through these studies, the paper aims to develop high-performance zinc-based bearing alloys suitable for various application scenarios, especially those requiring high strength and high wear resistance for large bearings.