Superhydrophobic β-Sialon-mullite ceramic membranes with high performance in water treatment

Feihong Wang,Binbin Dong,Nianwang Ke,Mingye Yang,Ruochan Qian,Junwei Wang,Junling Yu,Luyuan Hao,Liangjun Yin,Xin Xu,Simeon Agathopoulos

DOI: https://doi.org/10.1016/j.ceramint.2020.11.200

IF: 5.532

2021-03-01

Ceramics International

Abstract:<p>β-Sialon membranes with high mechanical strength and suitable porosity were prepared by pressureless sintering of samples obtained via phase-inversion and tape-casting and methods, and then their surface was modified with mullite whiskers through vapor-phase growth technology. Mullite whiskers, with a small diameter of ~100 nm and a high aspect ratio of ~30, were formed at the surface of the asymmetrically structured membrane. The prepared membrane exhibited high performance in separating of an aqueous emulsion of oil, (i.e. when the average diameter of the droplets of oil was 1.62 μm, oil rejection reached 94%). The mullite whiskers significantly increased the surface roughness of the membrane, leading, after surface modification, to superhydrophobicity (i.e. water contact angle was 165°), and to membrane distillation operational stability with 4% NaCl solution, containing 50 ppm humic acid, for more than 400 h. These results offer the prepared β-Sialon-mullite membranes excellent potential in the field of water treatment.</p>

materials science, ceramics

What problem does this paper attempt to address?

The main problem this paper attempts to address is the development of a β-Sialon-mullite ceramic membrane with high mechanical strength and surface roughness to enhance its performance in water treatment, particularly in applications such as oil-water separation and membrane distillation.

Specifically, the researchers prepared the β-Sialon ceramic membrane through methods such as pressureless sintering, phase inversion, and tape casting, and modified its surface with mullite whiskers using vapor growth technology. These mullite whiskers significantly increased the membrane's surface roughness, resulting in superhydrophobicity (water contact angle reaching 165°), and allowed it to operate continuously and stably for over 400 hours under conditions containing 4% NaCl solution and 50 ppm humic acid. These results indicate that the prepared β-Sialon-mullite ceramic membrane has excellent potential in the field of water treatment.