Elevated temperature microstructural stability in Al-7Cu-0.5Mn-0.2Zr alloys through Ce addition: Enhanced coherent interfacial stability of cu-rich θ'/α-Al interface

Guodong Niu,Langjie Zhu,Wangrui Ren,Yu Wang,Houwen Chen,Jianfeng Wang,Jian Mao

DOI: https://doi.org/10.1016/j.matchar.2023.112908

IF: 4.537

2023-04-14

Materials Characterization

Abstract:In this study, Ce was added into Al-Cu-Mn-Zr alloys to investigate the effect of Ce atoms on θ' precipitates via HAADF-STEM (high-angle annular dark-field scanning transmission electron microscopy). The results showed that Ce atoms could enter the lattice of θ' precipitates to occupy the internal Cu atom sites. Moreover, the interfacial stability of Cu-rich θ'/α-Al matrix with Ce addition was also estimated by DFT (Density Functional Theory). The Cu-rich θ' precipitates with Ce occupation demonstrated a lower interface energy (0.27 J/m 2 ) than that of θ' precipitates without Ce occupation (0.45 J/m 2 ). In other words, Ce atoms could stabilize the intermediate metastable Cu-rich θ' precipitates and therefore enhance the coarsening resistance of θ' precipitates at elevated temperatures. The addition of 0.3Ce can enhance the aspect ratio and decrease the number density of θ' precipitates in the Al-7Cu-0.5Mn-0.2Zr alloy in the T7 state. As a result, the elevated temperature microstructural stability of θ' in Al-7Cu-0.5Mn-0.2Zr alloys with Ce addition can be improved via enhancing coherent interfacial stability of the Cu-rich θ'/α-Al interface.

materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing