Abstract:Polyethylene wax (PEW) has emerged as a commonly used material for maintaining the quality of wood. The emulsification of solid PEW before being injected into wood can effectively overcome the shortcomings of the high-temperature melting and injection process of solid PEW. The permeability of Eucalyptus ( Eucalyptus saligna ) and Mongolian Scotch pine ( Pinus sylvestris var. Mongolica ) to PEW emulsion in vacuum environment was investigated using impregnation tests, and steaming pretreatment and microwave irradiation pretreatment were applied. The small particle size and low viscosity of the PEW emulsion, whose median particle size was 0.256 μm and viscosity was 52.2 mPa s (at 60 r/s), facilitated its penetration into the wood capillary system. The weight percent gain (WPG) of Eucalyptus and Mongolian Scotch pine post impregnation in vacuum was positively correlated with both the vacuum-holding time and the impregnation temperature, but after 60 min of impregnation the WPG of both wood species decreased significantly. Both pretreatment methods could substantially improve the wood permeability and effectively promote the penetration of the PEW emulsion into the wood. The maximum WPG was achieved when Eucalyptus and Mongolian Scotch pine were respectively steamed for 80 min and 120 min. There was an increase of 0.24 times for the former and an increase of 0.53 times for the latter compared to unpretreated wood. Both species exhibited the highest WPG after water immersion for 60 min (with average moisture content close to their fibre saturation point) and microwave irradiation for 30 s, which was respectively 0.28 and 0.75 times higher than that of unpretreated wood. There was a significant variation in WPG between the two species with the same pretreatment method. The relatively lower density and better-developed capillary system of Mongolian Scotch pine allowed more efficient penetration of PEW emulsion. It is recommended that, considering the time cost and practical enhancement, microwave irradiation should be givenpriority to when pretreating wood.

Unraveling the permeation-enhancing effect of didecyl dimethyl ammonium chloride (DDAC) on poplar wood (Populus cathayana Rehd.)

Role of surface treatment on water absorption of poly(vinyl chloride) composites reinforced by Phyllostachys pubescens particles

High-pressure Densification and Hydrophobic Coating for Enhancing the Mechanical Properties and Dimensional Stability of Soft Poplar Wood Boards

Improved Water Repellency and Dimensional Stability of Wood via Impregnation with an Epoxidized Linseed Oil and Carnauba Wax Complex Emulsion

Chemical modification of poplar wood featuring compressible rebound 3D structure as water treatment absorbents

An Eco-Friendly Strategy of Cell Wall Stapling: in Situ Crosslinking of Acrylic Acid Emulsion Impregnated in Thermally Treated Poplar Wood

Imparting durable superhydrophobic/oleophobic properties to wood surfaces by means of PFDMS@MTCS vapor deposition

Improved Diffusivity of NaOH Solution in Autohydrolyzed Poplar Sapwood Chips for Chemi-Mechanical Pulp Production

Fabrication and performance of in-depth hydrophobic wood modified by a silica/wax complex emulsion combined with thermal treatment

Fabrication and mechanism analysis of wood polymer composites with improved hydrophobicity, dimensional stability and mechanical strength

Modification Mechanisms and Properties of Poplar Wood via Grafting with 2-Hydroxyethyl Methacrylate/N,N'-methylenebis(acrylamide) onto Cell Walls

Development of super dimensional stable poplar structure with fire and mildew resistance by delignification/densification of wood with highly aligned cellulose molecules

Effect of Impregnation with Maltodextrin and 1,3-Dimethylol-4,5-dihydroxyethyleneurea on Poplar Wood

Enhancement of the physical and mechanical properties of wood using a novel organo-montmorillonite/hyperbranched polyacrylate emulsion

Superamphiphobic plastrons on wood and their effects on liquid repellence

Improvement of decorative texture effects, thermal stability, and mechanical properties of Pinus massoniana using a combined dyeing and superhydrophobic modification method

Permeability of wood impregnated with polyethylene wax emulsion in vacuum

Modification of wood cell wall with water-soluble vinyl monomer to improve dimensional stability and its mechanism

Multifunctional Cellulose Wood with Effective Acoustic Absorption

Dimensionally stable and durable wood by lignin impregnation

Eco-friendly and Mildly Modification of Wood Cell Walls with Heat Treated Wood Extracts to Improve Wood Decay Resistance