Effect of the Cross Accumulative Roll Bonding on the Corrosion Behaviour of AA6082/AA7204 Composite Sheets

Manfa Yuan,Yunlai Deng,Sen Lin,Xiaobin Guo,Yuankang Xie

DOI: https://doi.org/10.1007/s12540-020-00865-9

IF: 3.451

2020-09-15

Metals and Materials International

Abstract:<span class="a-plus-plus abstract-section id-a-sec1"><p class="a-plus-plus">In this work, Al–Mg–Si/Al–Zn–Mg laminated composite sheets were successfully produced first time by combining AA6082 and AA7204 sheets through the cross accumulative roll bonding process. Two different starting materials were rolling bonded as alternate layers up to 8 rolling cycles with 408 °C pre-heating for 20 min before each cycle. In-situ corrosive surface was characterized by the electron backscattered diffraction to study the relationship between the grain orientation and the corrosion behavior of Al–Mg–Si/Al–Zn–Mg composite sheets. 78.2% of the volume fraction of S-type ({123} &lt;634&gt;) texture, 46.0% of R-Cubic-type ({001} &lt;110&gt;) texture and 18.8% of Brass-type ({110} &lt;112&gt;) texture reduced during in situ corrosive tests. Corrosion results indicated that the excellent corrosion resistance mainly contributed from grains near Brass-type texture ({110} &lt;112&gt;). As the volume fraction of the Brass-type ({110} &lt;112&gt;) texture distributed in the Al–Zn–Mg alloy around the interface increased from 0.18 to 4.16% with the rolling reduction increased from 93.7 to 99.2%, the corrosion resistance of the laminated rolling material improved.</p></span><span class="a-plus-plus abstract-section id-a-sec2 outputmedium-online"><h3 class="a-plus-plus">Graphic </h3></span>

materials science, multidisciplinary,metallurgy & metallurgical engineering