Abstract:We have made high surface area catalysts for the selective oxidation of methanol to formaldehyde. This is done in two ways - (i) by doping haematite with Al ions, to increase the surface area of the material, but which itself is unselective and (ii) by surface coating with Mo which induces high selectivity. Temperature programmed desorption (TPD) of methanol shows little difference in surface chemistry of the doped haematite from the undoped material, with the main products being CO2 and CO, but shifted to somewhat higher desorption temperature. However, when Mo is dosed onto the haematite surface, the chemistry changes completely to show mainly the selective product, formaldehyde, with no CO2 production, and this is little changed up to 10% Al loading. But at 15 wt% Al, the chemistry changes to indicate the presence of a strongly acidic function at the surface, with additional dimethyl ether and CO/CO2 production characteristic of the presence of alumina. Structurally, X-ray diffraction (XRD) shows little change over the range 0-20% Al doping, except for some small lattice contraction, while the surface area increases from around 20 to 100 m2 g-1. Using X-ray absorption spectroscopy (XAS) it is clear that, at 5% loading, the Al is incorporated into the Fe2O3 corundum lattice, which has the same structure as α-alumina. By 10% loading then it appears that the alumina starts to nano-crystallise within the haematite lattice into the γ form. At higher loadings, there is evidence of phase separation into separate Al-doped haematite and γ-alumina. If we add 1 monolayer equivalent of Mo to the surface there is already high selectivity to formaldehyde, but little change in structure, because that monolayer is isolated at the surface. However, when three monolayers equivalent of Mo is added, we then see aluminium molybdate type signatures in the XANES spectra at 5% Al loading and above. These appear to be in a sub-surface layer with Fe molybdate, which we interpret as due to Al substitution into ferric molybdate layers immediately beneath the topmost surface layer of molybdena. It seems like the separate γ-alumina phase is not covered by molybdena and is responsible for the appearance of the acid function products in the TPD.

In situ Mössbauer Spectroscopy Study of the Activation and Reducibility of Chromium- and Aluminium-doped Iron Oxide based Water-Gas Shift Catalysts under Industrially Relevant Conditions

In situ Mössbauer investigation of iron oxide catalyst in water gas shift reaction – Impact of oxyreduction potential and temperature

Revealing Structure-Activity Relationships in Chromium Free High Temperature Shift Catalysts Promoted by Earth Abundant Elements

Dynamics of CrO3–Fe2O3 Catalysts during the High-Temperature Water-Gas Shift Reaction: Molecular Structures and Reactivity

Nature of Reactive Oxygen Intermediates on Copper-Promoted Iron–Chromium Oxide Catalysts During CO2 Activation

Promotion Mechanisms of Iron Oxide-Based High Temperature Water–Gas Shift Catalysts by Chromium and Copper

Probing the Surface of Promoted CuO-Cr2O3-Fe2O3 Catalysts During CO2 Activation

A Mössbauer Study of In–Fe2O3/HZSM-5 Catalysts for the Selective Catalytic Reduction of NO by Methane

Alumina as a textural promoter of iron synthetic ammonia catalysts

Al-doped Fe2O3 as a support for molybdenum oxide methanol oxidation catalysts

The Reduction of Mg–Fe–O and Mg–Fe–Al–O Complex Oxides Studied by Temperature-Programmed Reduction Combined with in Situ Mössbauer Spectroscopy

Effects of Doping Rare Earth Elements (Y, La, and Ce) on Catalytic Performances of CoMo/MgAlM for Water Gas Shift Reaction

The Reduction Behavior of Fe-Mo-O Catalysts Studied by Temperature-Programmed Reduction Combined with in Situ Mössbauer Spectroscopy and X-Ray Diffraction

Ammonia-free Synthesis of Mo/CoMgAl Catalysts with Excellent Activities in Water-Gas Shift Reaction

In-Situ Dynamic Carburization of Mo Oxide with Unprecedented High CO Formation Rate in Reverse Water-Gas Shift Reaction

Effect of Stoichiometry and Method of Synthesis of Powdered Cu–Fe–Al Precursors on the Stability and Activity of CuFeAlO/CuFeAl Ceramometals in the High-Temperature Water Gas Shift Reaction

Reactive behaviors of iron-based shift catalyst promoted by ceria

Activation and Deactivation of the Commercial-Type CuO-Cr2O3-Fe2O3 High Temperature Shift Catalyst

The Influence of Cu and Al Additives on Reduction of Iron(III) Oxide: In Situ XRD and XANES Study.

A Structured Cu-Based/γ-Al2O3/Al Multifunctional Catalyst for Steam Reforming of Dimethyl Ether: Investigation on In-Situ CO Reduction Strategy

Optimizing Mo-C coordination for enhanced low-temperature water-gas shift activity over α-MoC 1-x catalysts: An experimental and theoretical study