Abstract:The reduction of Fe-based nanocomposite catalysts doped with Al and Cu has been studied using in situ X-ray diffraction (XRD), in situ X-ray absorption near-edge structure (XANES), and temperature-programmed reduction (TPR) techniques. The catalysts have been synthesized by melting of iron, aluminum, and copper salts. According to XRD, the catalysts consist mainly of Fe2O3 and Al2O3 phases. Alumina is in an amorphous state, whereas iron oxide forms nanoparticles with the protohematite structure. The Al3+ cations are partially dissolved in the Fe2O3 lattice. Due to strong alumina-iron oxide interaction, the specific surface area of the catalysts increases significantly. TPR and XANES data indicate that copper forms highly dispersed surface CuO nanoparticles and partially dissolves in iron oxide. It has been shown that the reduction of iron(III) oxide by CO proceeds via two routes: a direct two-stage reduction of iron(III) oxide to metal (Fe2O3 → Fe3O4 → Fe) or an indirect three-stage reduction with the formation of FeO intermediate phases (Fe2O3 → Fe3O4 → FeO → Fe). The introduction of Al into Fe2O3 leads to a decrease in the rate for all reduction steps. In addition, the introduction of Al stabilizes small Fe3O4 particles and prevents further sintering of the iron oxide. The mechanism of stabilization is associated with the formation of Fe3- xAl xO4 solid solution. The addition of copper to the Fe-Al catalyst leads to the formation of highly dispersed CuO particles on the catalyst surface and a mixed oxide with a spinel-type crystalline structure similar to that of CuFe2O4. The low-temperature reduction of Cu2+ to Cu0 accelerates the Fe2O3 → Fe3O4 and FeO → Fe transformations but does not affect the Fe3O4 → FeO/Fe stages. These changes in the reduction properties significantly affect the catalytic performance of the Fe-based nanocomposite catalysts in the low-temperature oxidation of CO.

Effect of Stoichiometry and Method of Synthesis of Powdered Cu–Fe–Al Precursors on the Stability and Activity of CuFeAlO/CuFeAl Ceramometals in the High-Temperature Water Gas Shift Reaction

The Impact of Stoichiometry and Method of Synthesis of Powder Cu–Fe–Al Precursor on Stability and Activity of Ceramometals CuFeAlO/CuFeAl in High Temperature WGSR

Impact of Incorporation of Active Nanoporous Components or Their Precursors in a CuAlO/CuAl Ceramometal Skeleton on the Properties in the Low-Temperature Water-Gas Shift Reaction

Effect of ceria on structure and thermostability of copper-iron-oxide catalyst

The Influence of Cu and Al Additives on Reduction of Iron(III) Oxide: In Situ XRD and XANES Study.

Activation and Deactivation of the Commercial-Type CuO-Cr2O3-Fe2O3 High Temperature Shift Catalyst

Stability of Pd-Cu-Cl-x/Al2O3 Catalyst for CO Oxidation

Strong Metal-Support Interactions Between Highly Dispersed Cu+ Species and Ceria Via Mix-Mof Pyrolysis Toward Promoted Water-Gas Shift Reaction

High and Stable Catalytic Activity of Ag/Fe 2 O 3 Catalysts Derived from MOFs for CO Oxidation

Effect of Co-fed Water on a Co-Pt-Si/γ-Al2O3 Fischer-Tropsch Catalyst Modified with an Atomic Layer Deposited or Molecular Layer Deposition Overcoating

Thermo-catalytic methane decomposition over unsupported Fe–Al and Co–Al catalysts for hydrogen and carbon nanostructures production

The Effect of Copper Addition on the Activity and Stability of Iron-Based CO2 Hydrogenation Catalysts

Preparation and Characterization of Fe/MgO Catalysts Obtained from Hydrotalcite-Like Compounds

Iron Cobaltite (FeCo2O4) Nanocatalysts for Water-Oxidation: Effects of Annealing Temperature on Catalytic Properties

Enhanced Activity of CuCeO Catalysts for CO Oxidation: Influence of Cu2O and the Dispersion of Cu2O, CuO, and CeO2.

Synergetic effects of Al addition on the performance of CoFe 2 O 4 catalyst for hydrogen production and filamentous carbon formation from direct cracking of methane

Polymer Nanofilm-Coated Catalysis: an Approach for Enhancing Water-Resistance of Co-Fe Oxide Nano-Catalysts under Moisture-Rich Condition

Dynamics of CrO3–Fe2O3 Catalysts during the High-Temperature Water-Gas Shift Reaction: Molecular Structures and Reactivity

Effects of Doping Rare Earth Elements (Y, La, and Ce) on Catalytic Performances of CoMo/MgAlM for Water Gas Shift Reaction

Revealing Structure-Activity Relationships in Chromium Free High Temperature Shift Catalysts Promoted by Earth Abundant Elements

Promotion Mechanisms of Iron Oxide-Based High Temperature Water–Gas Shift Catalysts by Chromium and Copper