Enhanced flux pinning by refined structural/magnetic domains in nickel-doped BaFe 2 As 2 single crystals

Yingjie Cui,Chiheng Dong,Caida Fu,Zhongtang Xu,Minghui Tang,Chengduo Wang,Yanwei Ma

DOI: https://doi.org/10.1016/j.mtphys.2023.101146

IF: 11.021

2023-06-10

Materials Today Physics

Abstract:The critical current density at high magnetic fields of high-temperature superconducting single crystals and films is mainly determined by the flux pinning force arising from interactions between fluxons and crystalline defects or secondary phases. However, iron-based superconductors, which are acknowledged as promising candidates for high-field applications, suffer from a lack of strong flux pinning centers. It leads to a critical current density ( J c ) inferior to that of iron-based superconducting films. In this work, we applied a simple annealing method to tailor flux pinning structures in slightly underdoped BaFe 2-x Ni x As 2 single crystals without significantly compromising superconductivity. We propose that the probable strengthened orthorhombic distortion by post-annealing could generate twin domain boundaries or short-range antiferromagnetic clusters with sizes comparable to the in-plane coherence length. The inclusion of the structural/magnetic structures enhances electron scattering but also provides potent flux pinning centers. Ultimately, the J c is enhanced by 2.5 times in the samples with optimized pinning landscapes. Our studies highlight the importance of further exploring underdoped iron-based superconductors, in which magnetic/orthorhombic phases that compete and coexist with superconductivity may also act as effective pinning centers.

materials science, multidisciplinary,physics, applied