Effect of surface-treated paddy straw biosilica additive on PET core–pineapple fiber composite subjected to water and temperature aging: a characterization study
N. Rajiv Kumar,R. Soundararajan,R. Srinivasan
DOI: https://doi.org/10.1007/s13399-024-06431-2
IF: 4.05
2024-12-17
Biomass Conversion and Biorefinery
Abstract:This study investigates the enhancement of mechanical properties in vinyl ester composites reinforced with silane-treated paddy husk biosilica and pineapple leaf fiber, even after undergoing aging processes. The novel use of modified paddy husk biosilica and silane-treated pineapple leaf fiber, combined with an aging process, forms the novelty of this work. Vinyl ester resin was chosen for its low shrinkage during curing, and methyl ethyl ketone peroxide (MEKP) was used as a catalyst. The amorphous biosilica is extracted from paddy straw and treated with silane to improve compatibility with the hydrophobic resin matrix. The hand layup method was used for composite fabrication, followed by curing at room temperature and post-curing at 120 °C. Subsequently, aging processes involved forcing the composites exposed to 40 °C and 60 °C hot air and warm water environments for 30 days. The mechanical properties of the composites were evaluated and revealed significant improvements. The specimen A2 exhibited superior performance across all tests, with a tensile strength of 114.8 MPa, flexural strength of 184.7 MPa, compression strength of 173.3 MPa, rail shear strength of 19.2 MPa, ILSS of 22.0 MPa, Izod impact strength of 6.2 J, and hardness of 80.8 Shore-D. In terms of water absorption, composite A2 showed 0.45%, indicating a slight reduction in hydrophobicity. It is further noted that the fatigue life of A2 is also significantly improved, with values of 34,049 cycles at 25% UTS, 30,515 cycles at 50% UTS, and 28,035 cycles at 75% UTS. In the drop load impact test, A2 absorbed 16 J of energy and showed a deflection of 2.0 mm, highlighting its excellent impact resistance. For flammability, composite A2 demonstrated a propagation speed of 9.3 mm/min and maintained a UL-94 V-0 rating with no falling drops or cotton ignition. Even after aging, composites B2 and C2 showed minimal reductions in mechanical properties. Composite B2, aged at 40 °C and 60 °C, maintained a tensile strength of 98.8 MPa, flexural strength of 164.2 MPa, and compression strength of 155.8 MPa. C2, aged in warm water, retained a tensile strength of 91.2 MPa, flexural strength of 145.2 MPa, and compression strength of 139.1 MPa. The SEM analysis provided further insights into the microstructural characteristics, showing uniform dispersion of biosilica particles and improved adhesion between the matrix and biosilica, contributing to superior mechanical properties. This study underscores the potential of bio-based fillers in developing high-performance composite materials suitable for various engineering applications.
energy & fuels,engineering, chemical