Abstract:More than one million tons of secondary aluminum dross as a hazardous waste are produced by aluminum manufacturers per year throughout the world, which imposes high disposal costs and serious environmental problems. As secondary aluminum dross is considered as an alumina-rich inorganic waste, this study aims to propose a promising approach for clean production of activated-alumina as a widely-used adsorbent, catalyst and catalyst support. In this paper, synthesis and characterization of high crystalline activated-alumina nanopowder from secondary aluminum dross using a novel five-step leaching-based process are presented. To optimize the process, various parameters of dross particle size, leaching time, leaching temperature, acid concentration, and liquid-to-solid ratio were studied using One-Factor-At-a Time approach (OFAT). For the following optimum leaching conditions: particle sizes between 38 and 75 μm, leaching time of 120 min, leaching temperature of 85 °C, acid concentration of 5 M, and the liquid-to-solid ratio of 20 ml/g, the extraction efficiency of alumina was around 83%. The leach liquor was purified by adding 2 N NaOH resulting in sodium aluminate-rich solution. The purified liquor was treated by adding HCl to precipitate Al(OH)3, and the Al(OH)3 was then washed and calcined at 700 °C for 2 h to obtain alumina. Chemical composition, mineralogical phases, chemical bonds, morphology, and particle size distribution of the as-synthesized activated-alumina were determined using X-ray fluorescence (XRF), X-ray diffractometry (XRD), Fourier transform infrared (FTIR) spectroscopy, field emission scanning electron microscopy (FESEM), and dynamic light scattering (DLS), respectively. The as-synthesized activated-alumina exhibited 97.61% purity. Its XRD pattern showed mainly characteristic peaks of gamma phase of alumina. Morphological study by FESEM revealed that the as-synthesized alumina particles have rounded-corner shape. The crystal and average particle size values were about 18.47 and 513 nm, respectively.

Production and modification of activated alumina

Mechanical Activation of Coal Fly Ash for the Improvement of Alumina–Silica Separation During Reduction Roasting–Alkaline Leaching Process

Extraction and Value-Added Utilization of Alumina from Coal Fly Ash Via One-Step Hydrothermal Process Followed by Carbonation

The Preparation and Modification of Active Alumina

Study on Preparation and Characterization of gamma-Al(2)O(3) from Coal Fly Ash

Comprehensive Extraction of Silica and Alumina from Coal Fly Ash via Reduced and Oxidized Roasting-Low Temperature Alkaline Leaching and Bayer Digestion

h of preparation of fi ne active alumina with high speci fi c surface area from sodium aluminate solution

Efficient Activation of Coal Fly Ash for Silica and Alumina Leaches and the Dependence of Pb(II) Removal Capacity on the Crystallization Conditions of Al-MCM-41

Effect of Pore Size Distribution of Carbon‐Covered Alumina on the Preparation of Submicrometer Α‐alumina Powders

PURIFICATION OF TAN RAI ALUMINUM HYDROXIDE WITH ACETIC ACID AND PREPARATION OF HIGH PURE NANOSIZE α-ALUMINA

A promising green process for synthesis of high purity activated-alumina nanopowder from secondary aluminum dross

Performance Optimization of Original Aluminum Ash Coating

Preparation of pseudo-boehmite via carbonation of sodium aluminate lixivium extracted from coal fly ash

Preparation And Characterization Of Gamma-Al2o3 By Polyaluminum Chloride With High Al-13 Content

A Study on the Coking Sites of Γ-Alumina Surface Using 1-Methylnaphthalene As the Model Reactant

EFFECT OF NH4HCO3 ON PORE STRUCTURE OF ALUMINA

Preparation and Characteristics of Polyaluminium Chloride by Utilizing Fluorine-Containing Waste Acidic Mother Liquid from Clay-Brine Synthetic Cryolite Process

Structure and phase changes of alumina produced by flame hydrolysis

Processing of Coal Fly Ash for the Extraction of Alumina Values

The activation mechanism of oxalic acid on γ-alumina and the formation of α-alumina