Suppression of hydrogen embrittlement of gear steel 20CrMnTiH with pulsed electric current

Yang Li,Xinfang Zhang

DOI: https://doi.org/10.1016/j.ijhydene.2023.03.079

IF: 7.2

2023-03-01

International Journal of Hydrogen Energy

Abstract:When steel is smelted and used, hydrogen penetration will lead to hydrogen embrittlement, reduce the service life of materials, and even cause safety accidents. Various defects in steel can trap hydrogen atoms as hydrogen traps, resulting in high hydrogen content in materials. In this study, 20CrMnTiH gear steel billets with high hydrogen content were treated by electric pulse. It was found that the elongation and tensile strength of the samples treated by electric pulse were improved, which is attributed to the reduction of diffusible hydrogen content in the sample. Meanwhile, as an irreversible hydrogen trap, FeO's reduction makes it easier for hydrogen atoms to diffuse and escape under the electric field. Pulse current not only promotes the diffusion of hydrogen atoms, but also eliminates some hydrogen traps. The hydrogen control method under pulse current provides another alternative for solid state dehydrogenation and repair of hydrogen embrittlement fracture.

energy & fuels,electrochemistry,chemistry, physical