Abstract:This paper investigated the influence of the electric pulses on the flow behavior and plasticity of the advanced high strength steel (AHSS) Dual Phase, DP980. In order to isolate the thermal effect of the electric pulses, two kinds of uniaxial tensile tests at the same testing temperature were carried out: (1) isothermal tensile test carried out in an environment cabinet and (2) electrically-assisted isothermal tensile test. The stress–strain curves were recorded and compared. The results indicate that at the same testing temperature, the stress–strain curves obtained by test (1) are generally lower than curves deserved by test (2). It demonstrates that electric pulses can not reduce the flow stress when compared with the case that without electric pulse which is contrary to the traditional electroplastic effect. Another result is that when the testing temperature is not more than 573K, the stress–strain curves obtained by both tests are higher than the tension curve in room temperature and the cases are opposite when testing temperature is more than 573K. In addition, the elongation improvement is not observed as well in the stress–strain curves. The difference between the two tests when compared the cross section shrinkage rate and the fracture elongation rate is not obvious. From another aspect to study the athermal effect of the electric pulse, tests with only varying the peak current density or pulse frequency at the same testing temperature were conducted. The results once again show that no evident difference between the stress–strain curves. It confirms that no athermal effect exists in DP980. However, with temperature elevated to 473K, the material is strengthened and then weakened as temperature exceeds 473K. Scanning electron microscope (SEM) analysis was adopted to better understand the observed phenomena. The results show that the decomposion of the martensite and the thermal effect are the main reason that attributes to the strength variation. Fracture surface morphology analysis indicates that the appearance of the shallower and smaller dimples as well as fracture platform represents the bad plasticity when increasing temperature. Meanwhile, fracture pattern is transformed from brittle fracture in test (1) to ductile fracture in test (2) when tensioned at 673K.

A novel electric pulse pathway to suppress plastic localization and enhance strain hardening of medium Mn steel

Effects of Electric Current Pulses on Mechanical Properties and Microstructures of As-Quenched Medium Carbon Steel

Realizing Strength–ductility Synergy in a Lean Duplex Stainless Steel Through Enhanced TRIP Effect Via Pulsed Electric Current Treatment

Achieving Stress Relief in Martensitic Stainless Steel Via High-Density Pulsed Electric Current Treatment

Unveiling Thermal and Athermal Effects in Strain Hardening Removal of A6061 Aluminum Alloy

Enhancement Of Fatigue Life And Elongation Of Metallic Materials By High-Density Pulsed Electric-Current

Relief of Strain Hardening in Deformed Inconel 718 by High-Density Pulsed Electric Current

Overcoming the Trade-off Between Strength and Ductility in Austenitic Stainless Steel Using a High-Density Pulsed Electric Current

Ultrahigh Deformability of Ti-6Al-4V Assisted by High-Density Pulsed Electric Current Treatment

Annealing Effect of High-Density Pulsed Electric Current Treatment on Cold-Rolled 6061 Aluminum Alloy

Effect of High-Density Pulsed Electric Current on the Formability of Aluminum Alloy

Experimental Investigation on a Novel Medium Mn Steel Combining Transformation-Induced Plasticity and Twinning-Induced Plasticity Effects

Microstructures of High-speed Deformation in 0.20% C Carbon Steel Induced by High-current Pulsed Electron Beams Irradiation

Stability of Martensite with Pulsed Electric Current in Dual-Phase Steels

Strengthening and Toughening of ZG25SiMn2CrB Steel without Tempering Brittleness via Electropulsing Treatment

Effects of hot/cold deformation on the microstructures and mechanical properties of ultra-low carbon medium manganese quenching-partitioning-tempering steels

Anomalous Dissolution Mechanism During Electropulsing-Assisted Solution Treatment Enhancing the Strength-Ductility Compatibility in Aermet 100 Steel

Plastic Deformation Caused by Pulsed Magnetic Treatment of Mid-Carbon Steel

The effect of electropulsing-assisted ultrasonic nanocrystal surface modification on the microstructure and properties of 300M steel

Experimental Investigation on Electroplastic Effect of Dp980 Advanced High Strength Steel

Effect of High Current Density Electropulsing on the Microstructure of Later-Serviced High Manganese Steel Crossing