Promoting effects of SO(4)(2-)on a NiMo/gamma-Al(2)O(3)hydrodesulfurization catalyst
Zhiwei Liu,Wei Han,Dawei Hu,Hong Nie,Zhen Wang,Shuling Sun,Zhonghuo Deng,Qinghe Yang
DOI: https://doi.org/10.1039/d0cy01004a
IF: 6.177
2020-01-01
Catalysis Science & Technology
Abstract:This study details the promoting effects that SO(4)(2-)has on a NiMo/gamma-Al(2)O(3)catalyst prepared using NiSO4(CAT-Sulf) as a nickel precursor, compared with the Ni(NO3)(2)(CAT-Nit) and the industrial NiMoP-complex (CAT-NiP) after 600 degrees C calcination. The three catalysts were characterized by virtue of X-ray diffraction (XRD), thermogravimetry mass spectrometry (TG-MS), N(2)adsorption-desorption, hydrogen temperature programmed reduction (H-2-TPR), X-ray photoelectron spectroscopy (XPS) and high-resolution transmission electron microscopy (HRTEM). Hydrodesulfurization (HDS) activity was assessed using dibenzothiophene (DBT) as the feedstock. On the one hand, compared with CAT-Nit, the SO(4)(2-)anions could be anchored on the catalyst surface due to their thermal stability and strong interaction with Al2O3, while few NO(3)(-)anions could be found. These anchored SO(4)(2-)anions weaken the metal-support interaction and hinder the formation of NiAl2O4, thereby facilitating both the sulfidation of Mo species and the decoration of Ni atoms and generating more Ni-Mo-S active sites. On the other hand, compared with CAT-NiP, the residual SO(4)(2-)anions do not impair the support properties and CAT-Sulf maintains excellent textural structure,i.e.high specific surface area and a proper pore structure. Therefore, CAT-Sulf exhibits the highest dibenzothiophene hydrodesulfurization (DBT-HDS) activity out of the three catalysts. Moreover, these anchored SO(4)(2-)anions effectively hinder the aggregation and growth of the active phases, thus guaranteeing a catalyst with high metal dispersion and good stability. Finally, using the inferior residual oil as a feedstock, the stability of CAT-Sulf was also assessed compared with an industrial catalyst (CAT-Ref), and the results show that during 1500 h on stream, its HDS ratio is maintained at around 78%, while that of the industrial catalyst (CAT-Ref) declined fromca.82% toca.71% after 1200 h, indicating that CAT-Sulf exhibits much better stability and shows excellent industrial potential. The anchored SO(4)(2-)anions simultaneously endow the NiSO4-derived catalyst with excellent physical structure, high intrinsic activity and good stability, indicating that it might be a simple and effective method to balance the activity and stability of the HDS catalyst using thermostable nickel precursor salts.