Development of Novel High Capacity Fluoride Ion Battery Cathode Utilizing Anion Redox of Sulfur
Zulai Cao,Yuki Orikasa,Kentaro Yamamoto,Toshiyuki Matsunaga,Toshiki Watanabe,Ryogo Ohashi,Shintaro Tachibana,Hidenori Miki,Kazuto Ide,Hideki Iba,Yoshiharu Uchimoto
DOI: https://doi.org/10.1149/ma2023-024721mtgabs
2023-12-22
ECS Meeting Abstracts
Abstract:All-solid-state fluoride-ion batteries (FIBs), which are based on the shuttling of fluoride ions, have been considered as one of the promising alternates for next-generation energy storage devices because of high theoretical energy density and safety. Benefiting from the multi-covalent fluorination process, metal/metal fluorides (M/MF x ) have been firstly utilized as electrode materials for FIBs with high theoretical energy densities. [1] However, M/MF x systems suffer from exceptionable volume expansion upon fluorination process due to the close-packed metal atoms, which would cause blockage of the F - diffusion pathway, resulting in devastating damage to the electrode-electrolyte interfaces. To solve these problems, cathode materials that utilize topotactic fluoride ion intercalation reactions, similar to the electrode materials applied in lithium-ion secondary batteries, are being developed. [2] Cathode materials that utilize topotactic intercalation of fluoride ions are often composed of heavier elements than the cathodes of lithium-ion batteries that use the same type of reaction mechanism, and effective anion redox is required if capacity is to be increased beyond that of lithium-ion secondary batteries.In this research, we investigated Sr 2 F 2 Fe 2 OS 2 (SFFOS) compound with a layered structure as a novel cathode material for all-solid-state FIBs, and evaluated its electrochemical properties and elucidated the charge compensation mechanism using anion redox of sulfur. SFFOS was synthesized by a solid-state reaction under vacuum environment using SrF 2 , SrO, Fe, and S. [3] SFFOS/La 0.9 Ba 0.1 F 2.9 /vapor grown carbon fiber (VGCF) was used as the composite cathode, La 0.9 Ba 0.1 F 2.9 as the electrolyte and Pb/PbF 2 / La 0.9 Ba 0.1 F 2.9 /VGCF as the composite anode to construct the electrochemical cell. Charge-discharge measurements were carried out in the cut-off voltage range of -1.5 to 1.5 V at 140°C. Ex-situ X-ray Diffraction (XRD), X-ray absorption spectroscopy (XAS) measurements of Fe K -edge, S K -edge, O K -edge and F K -edge were carried out under different state of charge during the 1 st and the 2 nd cycle. SFFOS showed reversible intercalation/de-intercalation of fluoride ions and a capacity of ~6.1 fluoride ions per unit cell (403 mAh g -1 ). The charge compensation mechanism was revealed for SFFOS by XAS measurements, where S redox contributed to the whole voltage range from -1.5 V to 1.5 V vs. Pb/PbF 2 , and Fe +2/+3 redox contributed from the middle SOC. The S-S dimers were formed upon charging, which was similar to the trapped O 2 molecules observed in lithium-excess metal oxide during charge process [4] . Not only can the F - anions insert around Fe to form Fe-F bonds, but the excess F - anions can also occupy the Sr-S interstitial layers in the original lattice. Compared to the Fe-based layered oxide Sr 3 Fe 2 O 5 , the Fe-based oxysulfide SFFOS showed a lower average voltage but a higher specific capacity. We believe that this study could provide a new understanding of sulfur-based charge compensation and electrochemical fluorination reactions. Reference s : [1] D. Zhang, K. Yamamoto, Y. Uchimoto et al. , J. Mater. Chem. A , 2021, 9, 406–412. [2] Y. Wang, K. Yamamoto, Y. Uchimoto, et al. , Chem. Mater. , 2022, 34, 609–616. [3] Kabbour H, Janod E, Corraze B, et al . , J. Am. Chem. Soc. , 2008, 130(26): 8261-8270. [4] R. A. House, P. G. Bruce, et al. , Nat. Energy 2020, 5, 777–785. Figure 1