Abstract:Regular grain oriented (RGO) silicon steels (0.18, 0.23, and 0.28 mm thick) with forsterite coating were formed into 37.2 and 63.6 kg uncut toroids, gapped toroids, and gapped, pressed rectangular cores. During the core (or toroid) manufacturing process, samples of the steel were obtained for Epstein testing at the front and back ends of each core or toroid. The cores/toroids and Epsteins were stress relief annealed at 800° for 4 hours in an 85% nitrogen - 15% hydrogen atmosphere. Additionally, gapped rectangular cores were made from forsterite-coated and stress-coated 0.18, 0.23, and 0.28 mm RGO silicon steels and 0.23 mm stress-coated high-permeability oriented (HGO) silicon steels. Process Factors (PF) were calculated by the equation: PF (%) = \frac{W(core) - W(Epst)}{W(Epst)} \times 100 % For pressed rectangular cores made from RGO steel the process factors improve (i.e. become more negative) with decreasing steel thickness at a given test induction. Comparing gapped rectangular cores, gapped toroids, and uncut toroids, the most negative process factors were obtained in the uncut toroid, reaching as low as about -10% for the 0.18 mm and 0.23 mm RGO steels. For pressed rectangular cores, the high permeability oriented (HGO) silicon steels experienced more positive process factors than the regular grain oriented (RGO) silicon steels. At 1.7T the 29.0Kg cores made from 0.23 mm stress-coated HGO steel had an average process factor of +8.2% while the cores made from stress-coated RGO steel had an average process factor of -1.1%. The differences in core loss seen between Epstein tests of regular grain oriented (RGO) steels and high-permeability grain oriented (HGO) steels are not as large in transformer cores. For transformer manufacturers designing to high loss evaluations (i.e., lower design inductions), RGO steels may be the steels of choice, particularly 0.18 mm thick steel at inductions below 1.5T.

Condition assessment of transformer core CRGO steels due to thermal ageing and their evaluation

Research on Deterioration Mechanism of Oil-paper Insulation of 220 Kv Current Transformer

Amorphous Core Distribution Transformer with Improved Efficiency and Low Loss for Power Sector Application

Thermal prognosis of dry-type transformer: Simulation study on load and ambient temperature impacts

Process factors of transformer cores made from 0.18 mm, 0.23 mm, and 0.28 mm thick grain oriented steel

Vibration and Noise Measurement of medium-high frequency Transformer Cores under Non-Sinusoidal Excitation

Texture evolution in grain-oriented electrical steel during hot band annealing and cold rolling

Evolutions of microstructure and magnetic properties of heatproof domain-refined silicon steel during annealing and its application

Cyclic Softening Properties of 30cr2mov Steel at Elevated Temperatures

Temperature Rise Calculation of Magnetic Core Considering the Temperature Effect of Magnetic Properties in an Electrical Steel Sheet

Review of condition assessment of power transformers in service

Analysis of Magnetic Performance and Magnetostrictive Properties of Grain-Oriented Electrical Steels under DC Bias Condition

Electromagnetic Field Analysis and Optimization Method of High-Temperature Superconducting Transformer under the Influence of Abnormal Voltage

Optimization of hot rolling parameters of CRNO steel with the aid of hot compression test and deformation map

Influence of heat on the performance of stack welded thin sheets of CRNGO electrical steel

Thermal aging of FeCuNbSiB nanocrystalline materials under DC magnetic field

Life Monitoring and Evaluation Strategy of Traction Transformer on Freight Line

Micro characterization of aged liquid silicone rubber used for 220kV current transformer jacket

Practical Study of Mixed-Core High Frequency Power Transformer

Thermal response and failure mode evaluation of a dry-type transformer

Iron Loss and Temperature Rise Analysis of a Transformer Core Considering Vector Magnetic Hysteresis Characteristics under Direct Current Bias