Anticorrosion and Hydrophobic Surface Protection Inducing Dendrite‐Free Zn Anode for Aqueous Zn‐Ion Batteries

Chen‐Yang Li,Dong‐Ting Zhang,Hao Chen,Min‐Peng Li,Chen‐Yang Tian,Mao‐Cheng Liu

DOI: https://doi.org/10.1002/ente.202300885

IF: 4.149

2023-10-23

Energy Technology

Abstract:The time‐voltage curves of constant current Zn plating/stripping for Zn//Zn and PVDF‐SiC@Zn//PVDF‐SiC@Zn symmetrical batteries (different thickness of PVDF and SiC) at 0.5 mA cm−2 with a plating capacity of 0.25 mAh cm−2. Zinc is widely used as an anode in zinc‐ion batteries (ZIBs) due to its nontoxicity, favorable theoretical specific capacity, and low oxidation–reduction potential. Nevertheless, irreversible Zn dendritic growth and unavoidable side reactions limit its cyclic stability and high‐rate capability. This research puts forward a surface protection strategy by introducing a hydrophobic polyvinylidene fluoride and carborundum nanocoating (PVDF‐SiC) coating on the surface of Zn anode to synergistically restrain side reactions and Zn dendrites. PVDF improves the hydrophobicity of Zn anode at the solid–liquid interface, which can avoid side reactions between Zn anode and water. SiC nanoparticles with high porosity and small size pore can also homogenize the Zn2+ flux, which can cause uniform Zn deposition and inhibit Zn dendrite growth. The hydrophobic PVDF‐SiC@Zn symmetric battery accordingly exhibits an invariable overvoltage (<40 mV) after 780 h at 1 mA cm−2 with 0.25 mAh cm−2. Simultaneously, constant and convertible Zn deposition in PVDF‐SiC@Zn//Ti asymmetric battery is implemented. The PVDF‐SiC@Zn//V2O5 full battery exhibits 68% capacity retention after 400 cycles. The porous/hydrophobic PVDF‐SiC composite modification efficiently restrains the side reactions and Zn dendrite growth on the Zn anode, providing an innovative idea for achieving long‐life ZIBs.

energy & fuels

What problem does this paper attempt to address?

The paper aims to address several key issues in zinc-ion batteries (ZIBs), specifically including:

1. **Zinc Dendrite Growth**: Due to the uneven electric field distribution on the surface of the zinc anode, zinc ions preferentially deposit in areas with high electric field intensity, forming small protrusions, which in turn trigger uncontrollable zinc dendrite growth. These dendrites gradually grow and pierce the separator, causing internal short circuits and ultimately leading to battery failure.

2. **Side Reactions**: Zinc metal has low thermodynamic stability in aqueous electrolytes. Oxygen and water spontaneously react with the surface of the zinc anode, generating by-products (such as Zn₄SO₄(OH)₆·H₂O). These loose and insulating by-products cause passivation of the anode surface, reducing the utilization rate of zinc metal, thereby affecting the reversibility and cycle life of the battery.

To solve the above problems, the paper proposes a surface protection strategy by introducing hydrophobic polyvinylidene fluoride (PVDF) and silicon carbide nanocoating (SiC) on the surface of the zinc anode, synergistically inhibiting side reactions and zinc dendrite growth. PVDF can enhance the hydrophobicity of the zinc anode at the solid-liquid interface, preventing the zinc anode from contacting water, thereby reducing side reactions; while the high porosity and small pore size of SiC nanoparticles can homogenize the flux of zinc ions, promoting uniform zinc deposition and inhibiting zinc dendrite growth.

Through this strategy, the research team successfully achieved a stable, dendrite-free zinc anode and significantly improved the electrochemical performance and cycle life of zinc-ion batteries. Experimental results show that after 780 hours of cycling tests, the modified zinc anode still maintained stable overpotential (<40 mV) and exhibited excellent cycling stability and capacity retention in full-cell tests.