Dendrites‐Free Zn Metal Anodes Enabled by an Artificial Protective Layer Filled with 2D Anionic Nanosheets

Ying Zhang,Ming Zhu,Guanyao Wang,Fei‐Hu Du,Fangfang Yu,Kuan Wu,Minghong Wu,Shi‐Xue Dou,Hua‐Kun Liu,Chao Wu

DOI: https://doi.org/10.1002/smtd.202100650

IF: 12.4

2021-08-22

Small Methods

Abstract:Metallic zinc (Zn) has been considered to be an ideal anode material for aqueous batteries, but is impeded by the growth of Zn dendrites and its side reactions with an aqueous electrolyte. Here, it is reported that an artificial protective layer filled with novel 2D Zn2+ adsorbed Sb3P2O143− (denoted as Zn-Sb3P2O14) nanosheets provide an effective route to mitigate the above challenging problems. The Zn-Sb3P2O14 protection layer not only avoids the direct contact with the aqueous electrolyte to suppress the side reactions but also allows for Zn-ions to pass through the protection layer rapidly. Moreover, the 2D Sb3P2O143− skeleton with negative charge also confines the 2D diffusion of Zn-ion along the lateral surface of Zn anode, resulting in a uniform electron-deposition. This unique protection layer not only enables dendrite-free Zn plating/stripping with an average Coulombic efficiency of 99.2% for 200 cycles, but also sustains the symmetric Zn||Zn cell over 1300 h at 1 mA cm−2 and 1 mAh cm−2 as well as for 450 h at 10 mA cm−2 and 10 mAh cm−2. Such advantages bring high reversibility to full Zn batteries with MnO2 cathodes, which deliver a discharge capacity of 111.7 mAh g−1 after 1000 cycles.

materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology

What problem does this paper attempt to address?

The paper attempts to address two main issues faced by zinc metal anodes when used in aqueous electrolytes: the growth of zinc dendrites and the corrosion reaction between zinc and the aqueous electrolyte.

1. **Growth of Zinc Dendrites**:
- Zinc dendrites tend to grow during the charge-discharge process of the battery, penetrating the battery separator and causing internal short circuits, which pose serious safety hazards.

2. **Corrosion Reaction Between Zinc and Aqueous Electrolyte**:
- Corrosion reactions occur between zinc metal and the aqueous electrolyte, which continuously consume active zinc and the electrolyte, damaging the lifespan of zinc metal batteries.

To tackle these issues, researchers have developed an artificial protective layer filled with 2D Zn2+ adsorbed Sb3P2O143− (denoted as Zn-Sb3P2O14) nanosheets. This protective layer not only prevents direct contact between the zinc foil and the aqueous electrolyte, inhibiting corrosion reactions, but also restricts the lateral diffusion of zinc ions through its surface negative charge, promoting uniform zinc deposition, thereby effectively suppressing the growth of zinc dendrites.

Using this method, the research team achieved dendrite-free zinc deposition/stripping with an average Coulombic efficiency of up to 99.2%. In symmetric cells, the Zn@Zn-Sb3P2O14 electrode can stably cycle for over 1300 hours at 1 mA cm−2 and 1 mAh cm−2, and for over 450 hours at 10 mA cm−2 and 10 mAh cm−2. Additionally, when paired with a MnO2 cathode, the zinc metal anode with this protective layer can stably cycle 1000 times at 1 A g−1, demonstrating excellent cycle life.