Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Investigation of Carbon Steels (API 5L X52 and API 5L X60) Dissolution CO2–H2S Solutions in the Presence of Acetic Acid: Mechanistic Reaction Pathway and Kinetics

Electrochemical Investigation of the Corrosion Behavior of API 5L-X65 Carbon Steel in Carbon Dioxide Medium

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions

Corrosion Behavior of X52 Anti-H2S Pipeline Steel Exposed to High H2S Concentration Solutions at 90 °C

Effect of Temperature and H<sub>2</sub>S Concentration on Corrosion of X52 Pipeline Steel in Acidic Solutions

Corrosion Investigation of Commercially Available Linepipe Steel in CO2 Environment

Investigation of Supercritical CO2 Corrosion Behavior of X80 Carbon Steel in Pipelines: an in Situ Experimental and DFT Study

Synthesis and inhibitive characteristic of two acryloyl chloride derivatives towards the corrosion of API 5L X52 carbon steel in hydrochloric acid medium

Influence of FeCO 3 and FeSO 4 Layers on Corrosion in Sulfuric Acid Medium of Eutetoid Steels

Corrosion of N80 carbon steel in oil field formation water containing CO 2 in the absence and presence of acetic acid

Flow-Assisted Corrosion of API 5L X56 Steel: Effect of Flow Velocity and Dissolved Oxygen

Performance of two high-strength steels under electrochemical corrosive and stressed conditions

Technical Note: Electrochemistry of CO2 Corrosion of Mild Steel: Effect of CO2 on Cathodic Currents

Corrosion-Mechanical Properties and Susceptibility to Hydrogenetaion of Pipe Steel in the Presence of Carbon Dioxide Gas and Hydrogen Sulphide in Environment

Investigation of the Effect of pH on Stress Corrosion Cracking of API 5L X65 Steel by Impedance Spectroscopy and Slow Strain Rate Tensile Test

Effect of carbon dioxide on corrosion of tubular steel in high hydrogen sulfide and carbon dioxide environments

The Corrosion Behavior of Carbon Steel in CO2‐saturated NaCl Crevice Solution Containing Acetic Acid

Corrosion Performance of Carbon/stainless Steel in Amine‐based Solvents under Different Conditions for CO2 Chemical Absorption Process

Properties of Surface Film on XT0 Pipeline Steel in CO2-3/HCO-3 Environment

Effect of Pressure on Corrosion Behavior of X60, X65, X70, and X80 Carbon Steels in Water-Unsaturated Supercritical CO 2 Environments