A comprehensive study of Al-Cu-Mg system reinforced with nano-ZrO2 particles synthesized by powder metallurgy technique

Essam B. Moustafa,Abdulrahman Aljabri,Waheed S. Abushanab,E. Ghandourah,Mohammed A. Taha,Ahmed B. Khoshaim,Rasha A. Youness,S. S. Mohamed

DOI: https://doi.org/10.1038/s41598-024-53061-9

IF: 4.6

2024-02-05

Scientific Reports

Abstract:More focus has recently been placed on enhancing the strength, elastic modulus, coefficient of thermal expansion (CTE), wear and corrosion resistance, and other qualities of aluminum (Al) alloys by varying the quantity of ceramics added for a range of industrial uses. In this regard, Al-4.2-Cu-1.6Mg matrix nanocomposites reinforced with nano-ZrO 2 particles have been created using the powder metallurgy approach. The microstructure and particle size distributions of the produced powders were analyzed using a diffraction particle size analyzer, XRD, TEM, and SEM. To achieve good sinterability, the powders were compacted and sintered in argon. The sintered nanocomposites' mechanical, elastic, and physicochemical characteristics were measured. Additionally, the behavior of corrosion, wear, and thermal expansion were examined. The results showed a decrease in the particle sizes of the Al-Cu-Mg alloy by adding ZrO 2 nanoparticles up to 45.8 nm for the composite containing 16 wt.% ZrO 2 . By increasing the sintering temperature to 570 °C, the densification of nanocomposites was enhanced. Also, the coefficient of thermal expansion and wear rate remarkably decreased by about 28 and 37.5% by adding 16 wt.% ZrO 2 . Moreover, microhardness yield, strength, and Young's modulus were enhanced to 161, 145, and 64%, respectively, after adding 16 wt.% ZrO 2 . In addition, increasing the exposure time was responsible for decreasing the corrosion rate for the same sample.

multidisciplinary sciences

What problem does this paper attempt to address?

The paper aims to improve the performance of the Al-4.2Cu-1.6Mg alloy by adding nano ZrO₂ particles in varying proportions (up to 16% by weight). Specifically, the research objectives include:

1. **Enhancing mechanical properties**: By adding nano ZrO₂ particles, the mechanical properties such as hardness, compressive strength, and elastic modulus of the material are enhanced.
2. **Reducing the coefficient of thermal expansion**: By adding nano ZrO₂ particles, the coefficient of thermal expansion (CTE) of the material is reduced, thereby improving dimensional stability.
3. **Improving wear and corrosion resistance**: By adding nano ZrO₂ particles, the wear rate and corrosion rate of the material are reduced.
4. **Optimizing microstructure**: The composite material is prepared using powder metallurgy techniques, and its microstructure and particle size distribution are analyzed.

The research results indicate that after adding 16% by weight of nano ZrO₂, the microhardness, compressive strength, and Young's modulus of the material increased by 161%, 145%, and 64%, respectively, while the coefficient of thermal expansion and wear rate decreased by approximately 28% and 37.5%, respectively. Additionally, the corrosion rate also decreased. These improvements are significant for enhancing the application of aluminum alloys in the automotive, aerospace, and defense industries.